Manufacture of Wood-Pottery Composite Board

Manufacture of Wood-Pottery Composite Board. Andi Hermawan, Takeshi Ohuchi, Noboru Fujimoto, Yasuhide Murase Kyushu University-Japan. Introduction. Board evaluation. Prune wood. Three-layer composite board. Wood-Pottery Composite Board. Effective utilization.

altessa
Download Presentation

Manufacture of Wood-Pottery Composite Board

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Manufacture of Wood-Pottery Composite Board Andi Hermawan, Takeshi Ohuchi, Noboru Fujimoto, Yasuhide Murase Kyushu University-Japan

  2. Introduction Board evaluation Prune wood Three-layer composite board Wood-Pottery Composite Board Effective utilization Single-layer composite board Pottery stone scrap

  3. Window Specimen Meker burner Board after test Schematic diagram of incombustible properties test Evaluation of Board Properties • Physical and mechanical properties (JIS A 5908):Density, moisture content, bending test, internal bond test, thickness swelling test • Incombustible properties (JIS A 1322):After flaming time, glowing time, carbonization length, weight loss

  4. Properties of Wood-Pottery Composite Board • The board (three-layer) has excellent internal bond strength, thickness swelling and incombustible properties • Bending strength of the board was poor Therefore, improvement of bending properties of the board is necessary