1 / 9

As-Deposited Carbon

As-Deposited Carbon. After 3 hrs in 5µM GrBP2. Height (10 nm). 40 µm 2. 20 µm 2. As-Is Carbon on Si, no peptide. 500 nm 2. Height (5nm). Amplitude (0.10V). Phase (45°). Height (5nm). 25 µm 2. Amplitude (0.1V ). 2 µm 2. Phase (45°). As-Is Carbon After 3 hrs in 5µM GrBP2. 500 nm 2.

bran
Download Presentation

As-Deposited Carbon

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. As-Deposited Carbon After 3 hrs in 5µM GrBP2 Height (10 nm) 40 µm2 20 µm2

  2. As-Is Carbon on Si, no peptide 500 nm2 Height (5nm) Amplitude (0.10V) Phase (45°) Height (5nm) 25 µm2 Amplitude (0.1V) 2 µm2 Phase (45°)

  3. As-Is Carbon After 3 hrs in 5µM GrBP2 500 nm2 Height (5nm) Amplitude (0.10V) Phase (45°) Height (5nm) 5 µm2 Amplitude (0.10V) 2 µm2 Phase (45°) 1 µm2

  4. Annealed* Carbon After 3 hrs in 5µM GrBP2 500 nm2 Height (10nm5nm) Amplitude (0.10V) Phase (45°) Height (5nm) 20 µm2 Amplitude (0.10V) 2 µm2 Phase (45°) *anneal= 550°C for 1 hr

  5. Bare Si Substrate and After 2 hrs in 1µM/5µM GrBP2 bare silicon 2hrs, 1µM GrBP2 2hrs, 5µM GrBP2 5 µm2 Height (5nm) 500 nm2

  6. Summary Height (5nm) Height (5nm) Amplitude (0.10V) Phase (45°) As-Is 2µm2 As-Is w/Peptide Anneal w/Peptide 500 nm2

  7. Control 2-25-09 Marketa Peptide [c]=1mg/ml Peptide inc. O/N QD inc. 20 min GrBP2-dn (as-is C on Si) GrBP2-dn (annealed C on Si) 10m

  8. As-Is Carbon After FM with GrBP2-QD Height (10/5nm) Amplitude (0.10V) Phase (45°) 100 µm2 2 µm2 edge of carbon feature *sample very dirty after FM

  9. Quartz/Au Binding Peptide Project 10 µm T. Kacar 03-06-2009 Unmodified substrate HMDS-coated substrate Before experiment Before experiment After peptide and Gold NP assembly After peptide and Gold NP assembly