1 / 21

Monolithic Reactors for Environmental Catalysis

Monolithic Reactors for Environmental Catalysis. 朱信 Hsin Chu Professor Dept. of Environmental Eng. National Cheng Kung University. 1. Introduction. Minimize the pressure drop associated with high flow rates

doli
Download Presentation

Monolithic Reactors for Environmental Catalysis

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Monolithic Reactors for Environmental Catalysis 朱信 Hsin Chu Professor Dept. of Environmental Eng. National Cheng Kung University

  2. 1. Introduction • Minimize the pressure drop associated with high flow rates • Allow the process effluent gases to pass uniformly through the channels of the honeycomb

  3. 2. Chemical Kinetic Control • To be controlled by chemical kinetics rather than by diffusion to or within the catalyst pore structure while the geses are cold • When the surface becomes sufficiently hot, the rate will be determined by mass transfer. • In the laboratory, when screening a large number of catalyst candidates, it is important to measure activity at low conversion levels to ensure that the catalyst is evaluated in the intrinsic or chemical rate-controlling regime. • Good laboratory practice is to maintain all conversions below 20% for kinetic measurements. (adiabatic)For highly exothermic reactions (i.e., △H > 50kcal/mol), measurements should be made at conversions no greater than 10%.

  4. A material balance across any reactor gives the following equation assuming one-dimensional, plug flow, steady-state operation: where v = velocity (cm/s) C = molar concentration [(g‧mol)/cm3] z = length (cm) r = rate of reaction [(g‧mol)/(cm3‧s)] • When the conversion or the reactant concentration is low, the reactor is considerd isothermal; hence

  5. Assume the oxidation of ethane to CO2 and H2O in a large excess of O2 in a fixed bed of catalyst:We can assume that the rate is independent of O2. • It obeys first-order kinetics (pseudo-zero-order in O2), so the rate is expressed as:where k’ = the apparent rate constant • Integrating from the reactor inlet (i) to outlet (o) gives:where t = actual residence time (s)

  6. t = • Volumetric hourly space velocity (VHSV) VHSV = • The rate expression then becomes:By varying the space velocity, the change in conversion can be determined.The slop of the plot yields the k” of the reaction at STP. • Next slide (Fig. 4.1)Ethane conversion versus temperature at different space velocities.

  7. 3. Bulk Mass Transfer • When experiments are conducted with extremely active catalyst or at high temperatures, diffusional effects are introduced, and the intrinsic kinetics of the catalytic material is not determined accurately. • The activation energy will decrease as pore diffusion and bulk mass transfer become more significant. • Stationary environmental abatement processes are designed to operate in the bulk mass transfer regime where maximum conversion of the pollutant to the nontoxic product is desired. • Diffusion processes have small temperature dependency (low activation energies).Chemical-controlled reactions have a high degree of dependence on temperature (high activation energies).

  8. Important benefit of diffusion processes:the physical size and other geometric parameters of the honeycomb for a required conversion can be obtained using fundamental parameters of mass transfer.Where kg = mass transfer coefficient (cm/s) a = geometric surface area per unit volume (cm2/cm3) C = reactant gas phase concentration [(g‧mol)/cm3] • Integrating, Fractional conversion = 1- exp[-(kgat)]

  9. Some dimensionless numbers where D = diffusivity of pollutant in air (cm2/s) W = total mass flowrate to honeycomb catalyst (g/s) A = frontal area of honeycomb (cm2) dch= hydraulic diameter of honeycomb channel (cm)ρ = gas density at operating conditions (g/cm3) μ= gas viscosity at operating conditions (g/s‧cm) ε= void fraction of honeycomb, dimensionless • Equation on last slide becomes:Fractional conversion = 1- exp where L = honeycomb length (cm)

  10. Next slide (Fig. 4.2)Correlations for Nsh, Nsc, and NRe

  11. Example 1 Calculation for Mass Transfer ConversionThe removal of propane (C3H8) in a stream air at 300℃ and atmospheric pressure with:Flow rate, W= 1000 lb/h (126g/s)Diameter of monolith, D=6 in. (15.24 cm)Length of monolith, L=6 in.(15.24 cm)Area of monolith, A=182.4 cm2Monolith geometry, 100 cpsi (15.5 cells/cm2)C3H8 feed fraction, X=1000 vppm (volume parts per million) • Sol: From the literature (Lachman and McNally, 1985) dch = 0.083 in. (0.21cm) ε=0.69 a = 33 in.2/in.3 (13 cm2/cm3)

  12. Using Hodgman’s (1960) Handbook of Chemistry and Physics The density (ρ) and viscosity (μ) of air :ρ at 300℃ = 6.16 × 10-4 g/cm3μ at 300℃ = 297 × 10-6 g/s‧cmTherefore, • To utilize Fig. 4.2, the following term must be determined:

  13. From Bird et al., 1960, the diffusivity for a binary system:where M = molecular weight of species, A=air; B=C3H8 [g/(g‧mol] P = total pressure (atm)σAB= collision diameter for binary system (Å) T = absolute operating temperature (K) = collision integral for binary system, dimensionless • Using Table B-1 from Bird et al., 1960:For air: MA = 28.97, σA=3.617Å, For C3H8: MB=44.09, σB=5.061Å,where σ and are Lennard-Jones parameters for the single components.

  14. The binary system: • Using this value and Table B-2 from Bird (1960), • Therefore,

  15. Using Figure 4.2, NRedch/L=9.75→Nsh/Nsc0.56=3.8Therefore, Nsh=4.4 • Fractional conversion = = = 0.736 = 73.6% (done)

  16. 4. Reactor Bed Pressure Drop • Pressure drop (△P)a. flow contracts within the restrictive channel diameterb. washcoat on the surface of the honeycomb channel creates friction • The basic equation for △P derived from the energy balance:where P = total pressure (atm) f = friction factor, dimensionless gc = gravitational constant (980.665 cm/s2) υ= velocity in channel at operating conditions (cm/s) ρ= gas density at operating conditions (g/cm3) • Next slide (Fig. 4.3)Friction factor correlation to NRe

  17. The velocity in the channel (υ)where ε = void fraction (percent open frontal area of the honeycomb) A = cross-sectional area of honeycomb • Simplify the basic equation for △P • Next slide (Fig. 4.4) △P versus flow rate To select the optimum honeycomb geometry (volume, cross-sectional area, length, cpsi, etc.) for a given application