Part Name : Body Lower+Upper Report Date : 2012/8/2

Part Name : Body Lower+Upper Report Date : 2012/8/2. Material introduction. PC Makrolon 2607 Bayer MaterialScience. MFR:13 g/10 min. Analysis Indication. The distribution of thickness for this part is regular. The Fusion mesh is adopted for Moldflow CAE analysis model.

fergal
Download Presentation

Part Name : Body Lower+Upper Report Date : 2012/8/2

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Part Name : Body Lower+Upper Report Date : 2012/8/2

  2. Material introduction PCMakrolon 2607 Bayer MaterialScience MFR:13 g/10 min

  3. Analysis Indication • The distribution of thickness for this part is regular. • The Fusion mesh is adopted for Moldflow CAE analysis model.

  4. Feed System Design Layout:1 + 1 Sub gate:Ø2.0 mm

  5. Cooling System Design Same as the 2D mold drawing.

  6. Processing Conditions Filling Conditions: Melt temperature:300.00 deg.C Cooling Conditions: Coolant inlettemperature:90.00 deg.C Holding Setting(保压设定): Pressure(压力) [MPa] Duration(时间) [Second] 75 10

  7. Fill Time Fill time is 1.7 sec.

  8. Fill Time Shift+F5 Play this report file to view filling animation.

  9. Injection Pressure Left plot is the pressure distribution at the time of 99% filled(V/P switch over). The max. pressure is 124.6MPa.

  10. Clamp Force Clamp Force(锁模力)=80~100 Ton Higher hold pressures will increase the clamp force requirement.(保压压力越大,锁模力越大)

  11. Weld Lines No weld line

  12. Air trap The locations of air traps are shown as small pink balls.

  13. Air trap The locations of air traps are shown as small pink balls.

  14. Coolant Temperature The change in coolant temperature from coolant-in to coolant-out is not mare than 3°C .

  15. Mold Temp The mold temperature is uniform in the cavity. 定模温度均匀.

  16. Mold Temp The mold temperature is uniform in the core. 动模温度均匀.

  17. Time to Reach Ejection Temperature The acceptable range of time to reach eject-ion temperature for parts is 44~55 sec. Sink mark in the marked regions.

  18. Time to Reach Ejection Temperature Freeze time for gate is 10 sec. 浇口凝固时间为10秒.

  19. X Deflection The shrinkage is uniform in X direction. X

  20. Y Deflection The shrinkage is uniform in Y direction. Y

  21. Z Deflection 0.15 0.1 0.13 0.09 Z

  22. Summary Note: • The report is based on the analysis results of Moldflow Plastics Insight software. Please use this report for reference only.