An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Progress of ALD Group for MCP Qing Peng, Anil U. Mane, Jeffery W. Elam Argonne National Laboratory Third week of September 2009

  2. Aluminum doped Zinc Oxide (AZO) growth rate at different conditions 1/5/1/5 s, 20% ALO cycle Diethyl Zinc Trimethyl Aluminum • Results: • At 200C, with O3 chemistry AZO growth rate is smaller than the growth rate with H2O chemistry for same cycle conditions. • For H2O chemistry, AZO growth rate is smaller at 200C than at 177C

  3. Results of AZO coated MCP • Purpose: ALD2 system, coat AZO onto MCP with Si wafers as the control sample. • Conditions • Reaction temperature: 177C • Substrate: • Silicon with unknown resistivity, treated by Acetone/IPA, Then O3 for ~3 minutes. • MCP treated with O3 for ~3 minutes • Cycle conditions (dose/purge/dose/purge): 1/5/1/5 s for both Al2O3 and ZnO, • Cycle Numbers: 800 Cycles • Reactants: TMA/H2O for Al2O3, DEZ/H2O for ZnO. • Substrates: MCP 33 in diameter, IPN: 300-2592-A, polished AND Si wafers with unknown resistivity MCP+100nm AZO+Cr 5nm+Au 50nm Uncoated MCP MCP 100nm AZO

  4. Work has been done: • ALD process for AZO is carrying out, • Mercury probe and pico-ammeter for resistant measurement set up • Low resistivity Si wafer ordered • Sample holder for electrode coating is designed. Mercury probe and Pico-ammeter is set up for measuring high resistant • Work for near future: • Systematic study of ALD process for AZO for the optimal material property. • Automatic measuring system for resistance