Nové vysokoteplotné supravodiče na báze železa - pniktidy

Nové vysokoteplotné supravodiče na báze železa - pniktidy. Zuzana Pribulová Ústav experimentálnej fyziky SAV Košice. 10.12.2009. Pniktidy na báze železa. objavené začiatkom roku 2008. NdFeAsO(F), 2008. 10.12.2009. Pniktidy na báze železa. Niekoľko typov:. 10.12.2009.

oren-ochoa
Download Presentation

Nové vysokoteplotné supravodiče na báze železa - pniktidy

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Nové vysokoteplotné supravodiče na báze železa - pniktidy Zuzana Pribulová Ústav experimentálnej fyziky SAV Košice 10.12.2009

  2. Pniktidy na báze železa objavené začiatkom roku 2008 NdFeAsO(F), 2008 10.12.2009

  3. Pniktidy na báze železa Niekoľko typov: 10.12.2009

  4. Pniktidy vs. kupráty • magneticky usporiadaná materská zlúčenina • supravodivosť sa objavuje po dopovaní • - symetria energetickej medzery • počet energetických medzier • anizotropia Podobnosti Rozdiely H. Luetkens, et al., arXiv:0806.3533. Chen et al., EPL, 85 (2009) 17006 10.12.2009

  5. Mikrokontaktová spektroskopia Lokálna magnetizácia ac-kalorimetria balistický mikrokontakt N Cu ihla S T Tac Tb+Tdc t Tb P0 Tac = K + jCw SC Experimentálne metódy Teória BTK: dI/dV = f(D,G,z) Energetické medzery Hc1, Hirr Hc2 10.12.2009

  6. Mikrokontaktová spektroskopia NdFeAsO0.9F0.1(1111) Dve energetické medzery: 2D1/kBTc = 2.60.1 and 2D2/kBTc = 5.70.5 @ Samuely et al., Supercond. Sci. Tech. 22 (2009) 014003. 10.12.2009

  7. Mikrokontaktová spektroskopia NdFeAsO0.9F0.1(1111) @ Samuely et al., Supercond. Sci. Tech. 22 (2009) 014003. 10.12.2009

  8. Mikrokontaktová spektroskopia Ba0.55K0.45Fe2As2(122) Dve energetické medzery: 2D1/kBTc = 2.70.1 and 2D2/kBTc = 9.30.5 @ Szabóet al., Phys. Rev. B79 (2009) 012503. 10.12.2009

  9. Lokálna magnetizácia a ac-kalorimetria NdFeAsO0.9F0.1(1111) AnizotropiaHc2~ 5.5  1.5 Veľká oblasť kvapaliny vírov @ Pribulováet al., Phys. Rev. B79 (2009)020508(R). 10.12.2009

  10. Lokálna magnetizácia a ac-kalorimetria Ba0.55K0.45Fe2As2(122) AnizotropiaHc2~ 2 - 3 Oblasť kvapaliny vírov podstatne menšia Ireverzibilné mag. polia: @ Kačmarčíket al., Phys. Rev. B80 (2009)014515. 10.12.2009

  11. Zhrnutie Dve energetické medzery: malá s 2D/kTc ~ 2.6 veľká s 2D/kTc ~ 5.7 AnizotropiaHc2 ~ 5.5 1.5 Pravdepodobne veľká oblasť kvapaliny vírov NdFeAsO0.9F0.1 Dve energetické medzery: malá s 2D/kTc ~ 2.7 veľká s 2D/kTc ~ 9.3 AnizotropiaHc2 ~ 2 - 3 Ba0.55K0.45Fe2As2 10.12.2009

  12. 10.12.2009

  13. ďakujem 10.12.2009