Talc Mg 3 Si 4 O 10 (OH) 2

Phyllosilicates: Talc and Pyrophyllite. Pyrophyllite Al 2 Si 4 O 10 (OH) 2. Talc Mg 3 Si 4 O 10 (OH) 2. Crystallographic properties of talc and pyrophyllite. pyrophyllite 1Tc talc 1Tc space group P-1 P-1 a (Å) 5.160 5.290 b (Å) 9.966 9.173 c (Å) 9.347 9.460

aimee
Download Presentation

Talc Mg 3 Si 4 O 10 (OH) 2

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Phyllosilicates: Talc and Pyrophyllite Pyrophyllite Al2Si4O10(OH)2 Talc Mg3Si4O10(OH)2

  2. Crystallographic properties of talc and pyrophyllite pyrophyllite 1Tc talc 1Tc space group P-1 P-1 a (Å) 5.160 5.290 b (Å) 9.966 9.173 c (Å) 9.347 9.460 a(º) 91.18 90.46 b(º) 100.46 98.68 g(º) 89.64 90.09 V (Å3) 424.84 453.80 r (g/cm3) 2.72 2.80 Interlayer separation (Å) 2.759 2.832 Sheet thickness (T) 2.153 2.176 Sheet thickness (O) 2.079 2.168 Octahedral angle (º) 57.1 61.5 (M1) 61.5 (M2) (ideal) 54.73 54.73 (Lee and Guggenheim 1981, Perdakatsis and Burzlaff 1981)

  3. c-axis projection of T-O-T sheet in talc. Light green - Mg1, Dark Green - Mg2, Blue - Si, Red - O, small spheres - H (Perdikatsis and Burzlaff 1981)

  4. T-O-T layers in 2M talc. Silica tetrahedra are distorted with coplanar basal oxygens. Light green - Mg1, Dark green - Mg2, rlue - Si, red - O, small blue spheres - H (Evans and Guggenheim 1988)

  5. c-axis projection of a single T-O-T layer in 1Tc pyrophyllite. Al - orange, Si - blue, O - red, OH - pink. (Lee and Guggenheim 1981)

  6. T-O-T layers in 1Tc pyrophyllite. Note that the basal oxygens are slightly noncoplanar. Al - orange, Si - blue, O - red, OH - pink. (Lee and Guggenheim 1981)

  7. Layer Stacking • Not constrained by intelayer cations (as in micas) or hydrogen bonding. • Empty cation sites between layers are large and irregular, therefore the structure is distinct from a cation-deficient mica • Stacking disorder is ubiquitous, therefore it is not worthwhile to differentiate between polytypes generally between crystals • T-O-T layers are shifted by approximately 0.3ato minimize Si - Si repulsion • Common polytypes are 2M for talc and 1Tc for pyrophyllite, however 22 pyrophyllite polytypes and 10 talc polytypes are known, only some of which can be identified by x-ray analysis (Durovic and Weiss 1979, Bailey 1984)

  8. Chemistry of talc and pyrophyllite Talc: • Possible complete series with minnesotaite (Fe3Si4O10(OH)2) • Minor Al substitution for Si, no more than 4% • Trace amounts of Mn, Ti, Ni, Cr, Ca, Na, K • Mssbauer studies indicate in hydrothermal talc all iron is Fe+3, while talc from weathering profiles can contain Fe+2 or Fe+3 • Small amount of Al can substitute for Si • Octahedral sites contain less > 95% Al, remainder being Fe+2, Fe+3, Mg, or Ti Pyrophyllite: Both talc and pyrophyllite are often found to be very pure in composition. Evans and Guggenheim 1988)

  9. Layer stacking in talc and pyrophyllite is not constrained by interlayer cations. Adjacent tetrahedral layers are offset approximately 0.3a due to Si+4 repulsion. (Evans and Guggenheim 1988.)

  10. Occurrences of talc and pyrophyllite Talc: • High pressure metamorphic rocks rich in Mg but with low amounts of Al (chlorite), Ca (tremolite), and K (phlogopite) • Stable in surface environments as a precipitate over serpentine + quartz • Alteration product of olivine and orthopyroxene • Al-rich metamorphic rocks, much less common than talc Pyrophyllite:

  11. Thermal decomposition of talc and pyrophyllite • Talc undergoes rapid decomposition to enstatite + cristobalite + water at 600ºC (800ºC above 2kbar) • Pyrophyllite loses water and becomes pyrophyllite dehydroxylate above 450ºC. The structure contains under- and over-bonded oxygens and 5-coordination Al Mg3Si4O10(OH)2à 3MgSiO3 + SiO2 + H2O T = 400ºC

  12. Uses of talc and pyrophyllite • Used in the manufacture of ceramics • As a filler material in plastic, rubber, paint, insecticides, paper, and other materials • Made into acid and heat resistant laboratory countertops • Cosmetics and personal products • Used as an ornamental stone for carvings