材料試驗

破壞性 測試 黃瑞禮 49815046. 材料試驗. 金相(微結構)觀察. 取樣—金相切割機 鑲埋—熱鑲埋機 研磨—平面砂輪、水砂紙、雙盤研磨拋光機 拋光—機械拋光、電解拋光 浸蝕—化學腐蝕溶液 觀察—金相顯微鏡、電子顯微鏡. 金相切割機、熱鑲埋機. 雙盤研磨拋光機. 金相顯微鏡. 硬度試驗. 莫氏(劃痕)硬度 洛氏硬度（ HR A 、HR B 、HR C …） 勃氏硬度（ HB） 維氏硬度（ Hv） 微小硬度（ Hv、HK） 蕭氏硬度（ HS） 攜帶式硬度計：里氏硬度（ HL） 超音波量測. 洛氏硬度計. 微小維氏硬度計.

amir-hart
Download Presentation

材料試驗

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 破壞性測試 黃瑞禮 49815046 材料試驗 www.cnshu.cn 中国最大的资料库下载

  2. 金相(微結構)觀察 • 取樣—金相切割機 • 鑲埋—熱鑲埋機 • 研磨—平面砂輪、水砂紙、雙盤研磨拋光機 • 拋光—機械拋光、電解拋光 • 浸蝕—化學腐蝕溶液 • 觀察—金相顯微鏡、電子顯微鏡

  3. 金相切割機、熱鑲埋機

  4. 雙盤研磨拋光機

  5. 金相顯微鏡

  6. 硬度試驗 • 莫氏(劃痕)硬度 • 洛氏硬度（HRA、HRB、HRC…） • 勃氏硬度（HB） • 維氏硬度（Hv） • 微小硬度（Hv、HK） • 蕭氏硬度（HS） • 攜帶式硬度計：里氏硬度（HL） • 超音波量測

  7. 洛氏硬度計

  8. 微小維氏硬度計

  9. 硬度轉換對照表

  10. 拉伸測試 • 拉伸試驗是一種最普遍、最早使用的材料試驗方法 • 標準試棒拉伸測試 • 產品拉伸測試（釘槍、P79 frame等）

  11. 材料萬能試驗機

  12. 拉伸曲線 鋼鐵材料 非鐵材料 0.2% 降伏強度 抗拉強度 應力 塑膠 力量 脆性材料 應變 伸長量

  13. 疲勞試驗 • 材料受到重複施加的應力而斷裂，而每循環的應力強度皆小於該材料之降伏強度者，此種斷裂稱於疲勞斷裂 • 根據美國金屬學會（ASM）統計，機械的斷裂中有80~90%是材料疲勞的緣故

  14. 疲勞行為 • S-N曲線：S覆變應力，N疲勞生命週期 108 107 5*108

  15. 疲勞極限 • 非鐵金屬如鋁、鎂、銅等，不論應力如何降低，疲勞生命總有一定的極限 • 鐵、鈦等合金，在某一應力以下時，疲勞生命週期可達無限次，此一應力即稱為此材料之疲勞極限。工程上，假如材料在某一應力下週期次數達到107次或108次或者5* 108次也不斷裂，其中最大應力當作疲勞極限

  16. 疲勞斷面

  17. 疲勞斷面—壓鑄機車柱

  18. 疲勞斷面—壓鑄機車柱 斷裂方向