Sample THO10-017 観察

Sample THO10-017 観察. 分子の対称性としては C s 対称となり， ナノホーン上のアミドと同じであるので， むしろ 2 の方が結晶が観察されやすい可能性もある．. Sample preparation. ・ THO10-017 約 0.015 g を MtOH10ml に超音波分散（ 2 ｓ ×5 回）・・・（ a ） ・ (a) をＭｏグリッドに２滴 垂らし ろ 紙で吸い取る、真空中（ 6×10 -4 ）で完全に乾燥させる. Sample THO10-017 観察. 100331-11-8E. Low magnification. 2nm. 2nm.

anthony-nolan
Download Presentation

Sample THO10-017 観察

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Sample THO10-017観察 分子の対称性としてはCs対称となり， ナノホーン上のアミドと同じであるので， むしろ2の方が結晶が観察されやすい可能性もある． Sample preparation ・THO10-017約0.015gをMtOH10mlに超音波分散（2ｓ×5回）・・・（a） ・(a)をＭｏグリッドに２滴垂らしろ紙で吸い取る、真空中（6×10-4）で完全に乾燥させる

  2. Sample THO10-017観察 100331-11-8E Low magnification 2nm 2nm 2nm 2nm 全体的に観て、結晶の回折格子が観察される程度の大きさのナノ結晶は観察されなかった。 また、フラーレン様に丸くなった状態のものが多く観られた(hello01で丸くなる所が観られる) 全体から受ける印象としては、THO-09-080と同じというより、前回観察したTHO-01-004に似ている。

  3. Sample THO10-017観察 100330-11-8D High magnification helloV helloJ helloO helloP 2nm helloZ helloE helloG helloH helloi helloh 高倍率観察でも、結晶の様に規則的な重なりをもった 構造のものは観られない。 １～３分子が絡み合って基底分子に付いているように 見える。

  4. Sample THO10-017観察 100330-11-8D helloJ helloB hello01 2nm 2nm helloM helloN helloK 動きのある、かつ前回の試料では結晶構造をとった大きさのものを選んで動画を作成、 動きの中でも、結晶構造をとることは無かった。

  5. Sample THO10-017観察 100330-11-8D helloW helloT 2nm Ｒesult ひも状であったり、塊状であったり、何かついてはいるが 結晶らしいものは無い 面積を持っている類の物ではない 無し