1 / 2

!

Binary systems (binary sections). T, K. 3000. 2700. 2400. 2100. 1800. 1500. 1200. 900. 600. 300. x (mol). 0. 0.1. 0.2. 0.3. 0.4. 0.5. 0.6. 0.7. 0.8. 0.9. 1. CaO-UO 2. T, C. 2200. 1900. 1000. 2800. 2500. 1300. 1600. CaO. 20. 40. 60. 80. UO 2. mol.%.

bran
Download Presentation

!

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Binary systems(binary sections) T, K 3000 2700 2400 2100 1800 1500 1200 900 600 300 x (mol) 0 0.1 0.2 0.3 0.4 0.5 0.6 0.7 0.8 0.9 1 CaO-UO2 T, C 2200 1900 1000 2800 2500 1300 1600 CaO 20 40 60 80 UO2 mol.% CaO-UO2 ? ? ? ? ! ? ? + Alberman K.B. Blakey R.C. Anderson J.S. (1951) Roche M.F. Leibowitz L. Fink J.K. Backer Jr. (1993) Voronov N.M. Sofronova R.M. Ivanov O.S. (1972) Amato I. (1966) Holc J. Kolar D. (1986) CORPHAD project meeting

  2. Binary systems(binary sections) T, K T, C Phillips B. Muan A. (1958) 3000 2700 1700 2400 2100 ? 1800 1500 0.21105 Pa 1105 Pa 1500 1200 900 600 300 x (mol) 1300 0 0.1 0.2 0.3 0.4 0.5 0.6 0.7 0.8 0.9 1 CaO-FeO1.5 1100 900 CaO 60 70 80 90 Fe2O3 mass.% CaO-FeOy ? ? CORPHAD project meeting

More Related