Recent Advances in Modeling Fatigue in Metals

Recent Advances in Modeling Fatigue in Metals. Symposium in honor of C. Tome TMS, San Diego, February 28, 2011. H. Sehitoglu, M. Sangid,T. Ezaz, H.J.Maier University of Illinois, USA, University of Paderborn, Germany. Work Supported by Rolls Royce, National Science Foundation, DMR, Metals.

brandi
Download Presentation

Recent Advances in Modeling Fatigue in Metals

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Recent Advances in Modeling Fatigue in Metals Symposium in honor of C. Tome TMS, San Diego, February 28, 2011 H. Sehitoglu, M. Sangid,T. Ezaz, H.J.Maier University of Illinois, USA, University of Paderborn, Germany Work Supported by Rolls Royce, National Science Foundation, DMR, Metals

  2. Outline Modeling of Fatigue • Analysis of Grain Boundaries- Energy Barriers for G.B. Slip Transmission And G.B. Slip Nucleation • Energy Formulation for Crack Initiation via Persistent Slip Bands, Life results

  3. Fatigue Crack Initiation Experimentally observed mechanism: transgranular facets forming from persistent slip bands (PSBs) across GBs Sangid MD, Maier HJ, Sehitoglu H, “A physically-based model for prediction of crack initiation from persistent slip bands in polycrystals,” Acta Materialia 59 328-341 (2011).

  4. Atomic Simulations Use Molecular Dynamics Code, LAMMPs • Construct GBs from crystal lattices (axis/angle pairs) • Ni with Foiles-Hoyt EAM Potential: FCC Structure • 3D Periodic Boundary Conditions • Atoms ‘relax’ to determine grain boundary energy

  5. <001> Atomic Simulations of Prevalent Tilt & Twist GBs ( θ <110> ( <111> θ

  6. Mechanical Behavior of GBs: Slip Transmission A Σ3 (Twin) GB a/2 [011] t (100)t a/6 [211](111) Y [111] X [211] Z [011] Lomer Stair Rod Incident Sangid MD, Ezaz T, Sehitoglu H, Robertson IM, “Energy of slip transmission and nucleation at grain boundaries,” Acta Materialia 59 283-296 (2011).

  7. Contour Plot of Energy Barriers

  8. GB Energy Barriers to Slip • Monitor the energy of the atoms within a control box at the GB • Obtain the energy barrier for slip to penetrate the GB • Validated values of slip in a perfect FCC lattice by comparing with GSFE curve Error ~ 6%

  9. Measured Energy Barrier for Slip Transmission for various GBs

  10. Validation of MD Results of Slip Transmission

  11. Criterion for Slip Transmission Lee, Robertson, and Birnbaum, 1989 • Geometrical condition • Minimizes angle between lines of intersection of slip planes with GB, maximize M: • Resolved shear stress condition • After predicting active slip plane from GC, choose direction based on max resolved shear stress • Residual grain boundary dislocation condition • Minimize Burgers vector of residual dislocation (difference in b of incoming and outgoing ┴):

  12. Energy Barriers for Slip Transmission through GB

  13. Twin boundary has inherently high energy barriers for slip transmission Coherent twin boundary • Stable defect structure • Low static GB energy • High energy barrier for slip transmission • Note: • Applied loading is normal to GB • No applied shear stress on GB • General twin-slip interaction energies please refer to: Ezaz T, Sangid MD, Sehitoglu H, “Energy barriers associated with slip-twin interactions,” Philosophical Magazine, (2011). Slip is initially impeded by the twin resulting in a dislocation pile-up. As the applied load increases, slip transmits past the twin boundary. DOI: 10.1080/14786435.2010.541166

  14. Measured Energy Barrier for Slip Nucleation from various GBs

  15. Energy Barriers for Slip Nucleation from GB Please note: the Σ1,3,&11 GBs have a simple dislocation structure and stable configurations. Hence dislocations were nucleated in the matrix material during the simulation, preventing the energy barrier to be measured

  16. Fatigue Crack Initiation Experimentally observed mechanism: transgranular facets forming from persistent slip bands (PSBs) across GBs Sangid MD, Maier HJ, Sehitoglu H, “A physically-based model for prediction of crack initiation from persistent slip bands in polycrystals,” Acta Materialia 59 328-341 (2011).

  17. PSB Modeling and Energy Contributions • Model the energy of a persistent slip band through a physics based approach • Create an energy balance evolving with increasing loading cycles, which addresses all the PSB energy contributions: • Stress-field which must be overcome to have slip within the PSB • Applied Strain • Dislocation-dislocation interaction within the PSB (work-hardening) • Internal stress-field from dislocations • PSB interaction with GBs, particularly dislocations: • Piling-up at GBs • Nucleating from GBs and agglomerating within the PSB • Transmission through the GB • Formation of the PSB, dislocations shearing the γ matrix and γ’ precipitates • Crack initiates when PSB reaches minimum energy wrt to plastic deformation, i.e. dislocation motion

  18. Energy Formulation for a PSB MD Applied Work Work Hardening in Bands Dislocation Pile-ups Continuum Extrusion Formation at GBs Dislocation Nucleation at GBs Shearing of γ’ Precipitates Shearing of γMatrix where: σ≡ Applied stress h ≡ Width of PSB d ≡ Dislocation spacing ρ ≡ PSB dislocation density N ≡ Number of cycles m ≡ Schmid factor L ≡ Grain size Σ ≡ Characteristic of GB γ’ ≡ Distribution of precipitate L’ ≡ Grain size of neighboring grain Exp functions Microstructure Inputs Output Monitor a PSB and when it reaches a stable point, the material fails! Each term is expressed in terms of a slip increment, ∂X Sangid MD, Maier HJ, Sehitoglu H, “A physically-based model for prediction of crack initiation from persistent slip bands in polycrystals,” Acta Materialia 59 328-341 (2011).

  19. b = Burgers vector Energy associated with overcoming stress field within the PSB for motion of glissile dislocations where: L = grain size nlayers= number of dislocation layers in the PSB related to width of PSB, normalized by annihilation distance where the total stress is given by: Total stress Pile-up of dislocations Applied stress Lattice resistance ∂X= increment of slip Sangid MD, Maier HJ, Sehitoglu H, “A physically-based model for prediction of crack initiation from persistent slip bands in polycrystals,” Acta Materialia 59 328-341 (2011).

  20. PSB-GB Interaction Energy • Atomistic Based Formulation: • Dislocations nucleate from the GB and localize in slip bands • The number of dislocations that are emitted from the GB and aggregate within the PSB is given by: • PSBs form extrusions at grain boundaries in polycrystalline material • Leverage energy barriers for slip transmission and nucleation at a GB from atomic simulations (previously shown) Sangid MD, Maier HJ, Sehitoglu H, “The role of grain boundaries in fatigue crack initiation – an energy approach,” Accepted to International Journal of Plasticity (In Press - 2011).

  21. Energy due to shearing γmatrix and γ’ precipitates Stacking Fault Energy + Anti-Phase Boundary Energy Shearing of γ’ precipitates • Atomistic Based Formulation: where f is the area fraction of γ’, fU720~ 0.20 O M M’ O’ R Sangid MD, Maier HJ, Sehitoglu H, “A physically-based model for prediction of crack initiation from persistent slip bands in polycrystals,” Acta Materialia 59 328-341 (2011).

  22. PSB Energy Balance Sangid MD, Ezaz T, Sehitoglu H, Robertson IM, “Energy of slip transmission and nucleation at grain boundaries,” Acta Materialia 59 283-296 (2011). Sangid MD, Maier HJ, Sehitoglu H, “A physically-based model for prediction of crack initiation from persistent slip bands in polycrystals,” Acta Materialia 59 328-341 (2011).

  23. Criterion for Crack Initiation • Create an expression for energy (as energy components were previously shown) • Increment the number of loading cycles and update the energy expression as variables evolve: • Criterion for crack initiation • Energy of PSB reaches a stable value • Minimize energy to check for stability of PSB: where Xi represents the position of the glissile (mobile) dislocations in our energy expression Sangid MD, Maier HJ, Sehitoglu H, “A physically-based model for prediction of crack initiation from persistent slip bands in polycrystals,” Acta Materialia 59 328-341 (2011).

  24. More on PSB-GB Interaction θ> 15˚ θ< 15˚ PSBs transmit through low-angle GBs, θ < 15˚ High-angle GBs, θ > 15˚, impede dislocations, resulting in pile-ups, stress concentration, local increase in energy, and ultimately crack initiation TEM pictures from: Zhang & Wang, Acta Mat51 (2003).

  25. Clustering of grains Failure occurs due to PSB-GB interaction or Grain cluster (multiple grains connected by LAGBs) Single large grain

  26. Fatigue Scatter Results 1000 simulated specimens vs. 84 experimental results Each simulated specimen takes <30 seconds to construct its microstructure and predict fatigue life for a series of strain ranges Sangid MD, Maier HJ, Sehitoglu H, “An energy-based microstructure model to account for fatigue scatter in polycrystals,” Journal of the Mechanics and Physics of Solids (In Press - 2011).

  27. Conclusions • Atomistic Simulations • Quantified the strengthening mechanisms of slip transmission and nucleation from GBs • Inverse correlation between energy barrier and static interfacial energy • Lower GB energy results in a stronger barrier. • Fatigue modeling • Introduced methodology to model persistent slip bands energetics, in order to predict fatigue life. • Prediction of fatigue life • Accurately predict scatter in a deterministic framework