1 / 11

Our "SHIFT" #2

Our "SHIFT" #2. Globalisation ‘The missing link’. Major Quality Failure. The Failure. April 2008 cracking found in a Valve Body. Testing programme undertaken to assess chemical composition of all Work In Progress (1460 valves fitted on each submarine). Grain Size Problem. CONTAINMENT.

brielle-fischer
Download Presentation

Our "SHIFT" #2

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Our "SHIFT" #2

  2. Globalisation ‘The missing link’ Major Quality Failure

  3. The Failure • April 2008 cracking found in a Valve Body. • Testing programme undertaken to assess chemical composition of all Work In Progress (1460 valves fitted on each submarine).

  4. Grain Size Problem

  5. CONTAINMENT • Cause of cracking was the Manganese was below specification and in conjunction with excessive grain size was responsible for the failure. • Containment action initiated immediately to identify out of specification material and scale the size of the problem. • Three tier material assessment process established to check and confirm the acceptance of material. • Sort, using X-Ray fluorescence analysis (XRF) • Confirm material composition by analysing a scraping from below specification valve body determined by the XRF tool. • Detailed material analysis using sample sections from valve bodies.

  6. Source Mill India Make Bar Italy Manufacture UK T1 Supplier UK Make Bar France Forge Bodies Italy Submarine UK Stockist Germany Supply Chain Investigation

  7. Source Mill Investigation • The method of mixing the alloy in its molten state was not effective in ensuring the homogeneity throughout the ingot. • The extrusion procedure was inadequate and did not meet the NES requirements e.g. soak time and the reduction ratio were inadequate. • No control over calibration standards. • Wet Sample records and spectrometer results did not match. • Identification throughout the plant varied from permanent stamping to chalk which was considered inadequate and could result in loss of traceability. • C of C stated that material was annealed yet the company did not anneal that particular size

  8. Investigation Recommendations • Improve visibility of the entire supply chain. • Insist on original documentation accompanying transposed certificates. • Ensure appropriate balance of product verification and documentary evidence. (BS EN 10204:2004 Para 3.2 certification introduced) • Drive the development and modernisation of industry Quality Standards including MOD’s SSCP25 and ISO 9001 alternatives • Increase the use of commercial specifications e.g. define grain size • Continue with Positive Metal Indication (PMI) testing of in-coming material. Ensuring a safe quality product ………

  9. Any Questions?