直接通電による抵抗発熱を利用した 金属粉末の半溶融焼結

電極. 粉末. 電極. 直接通電による抵抗発熱を利用した 金属粉末の半溶融焼結. 目的 融点の違う金属粉末の混合粉を試料として , 通電焼結実験を行い , 半溶融焼結の可能性を調べた . 塑性加工研究室　 Soo Kean Leong. 通電時間　ｔ =1 ～ 3/s 圧粉圧力　ｐ =9.8 ～ 245.8/MPa 電圧　 E=5 ～ 8.5/V. 焼結条件. 圧粉圧力. 通電時間. 電流. 変圧器. 電極. 電圧. 粉末. AC. 電極. PC. 熱電対. 実験材料 電解銅粉 CE-25 アルミニウム Al-200mesh

calista
Download Presentation

直接通電による抵抗発熱を利用した 金属粉末の半溶融焼結

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 電極 粉末 電極 直接通電による抵抗発熱を利用した金属粉末の半溶融焼結 目的 融点の違う金属粉末の混合粉を試料として,通電焼結実験を行い,半溶融焼結の可能性を調べた. 塑性加工研究室　Soo Kean Leong

  2. 通電時間　ｔ=1～3/s • 圧粉圧力　ｐ=9.8～245.8/MPa • 電圧　 E=5～8.5/V 焼結条件 圧粉圧力 通電時間 電流 変圧器 電極 電圧 粉末 AC 電極 PC 熱電対 実験材料 • 電解銅粉 CE-25 • アルミニウム Al-200mesh • 鉄　Fe-S-200mesh • ニッケル　Ni-200mesh • 亜鉛　Zn-150mesh • Fe-Al50vol％ 粉末 ２００Ｖ 絶縁 コンテナ

  3. p=49MPa t =1.3s ρ:相対密度 (a)E=5V ρ=89.4% Al未溶融 (c)E=7V ρ=99.9% Al溶融 (b)E=6V ρ=97.8% Al半溶融 図　焼結体組織写真

  4. I 粉体 R VE トランス jωＬ r VL