An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. TECTOSILICATII

  2. TECTOSILICATII

  3. Grupa mineralelor SiO2

  4. Grupa mineralelor SiO2 • Transformari deplasative • Ajustari structurale la scara foarte mica ce necesita energie scazuta; • ex.: low Qtz - High Qtz la 573oC, deplasari reversibile ale legaturilor, fara a fi rupte

  5. Klein, Cap.13/pg.527/fig.13.114 • Polimorfii SiO2 1470 870 574

  6. Grupa mineralelor SiO2 Low Quartz 32 001

  7. Grupa mineralelor SiO2 High Quartz (581oC) 622 001

  8. Grupa mineralelor SiO2 Cristobalite 432 001

  9. Grupa mineralelor SiO2 Stishovite 4/mmm High pressure  SiVI

  10. Varietati microcristaline Calcedonia – varietate fibroasa, se depune din solutii agatul

  11. FELDSPATII -caracterizare chimica – procente moleculare ex. Or20Al75An5; -feldspatii de Ba – celsian, hialofan – in general rari. • Feldspati alcalini (K,Na)[AlSi3O8]; • Feldspati plagioclazi (Na,Ca)[Al1-2Si3-2O8]. • Feldspatii de Ba: • Celsianul – BaAl2Si2O8 • Hialofanul – (K,Ba)(Al,Si)2Si2O8 Proprietati fizice generale: -clivaj bun pe doua directii, cu unghi de ~90 sau apropiat; -duritate ~6; -greutate specifica 2.55-2.76 Na[AlSi3O8]→Ca[Al2Si2O8]

  12. FELDSPATII Modificatiile high-low Modificari structurale determinate de variatia temperaturii si a compozitiei: Doua tendinte de evolutie: Transformari deplasative – deformari structurale prin contractare datorate scaderii T° → scaderea simetriei 2/m→1; -tranzitie instantanee; -temperatura de tranzitie depinde de natura cationului. Transformariordine-dezordine -procesul de ordonare este extrem de lent; -implica ruperea si reorganizarea legaturilor Si-O si Al-O Transformari cuplate

  13. Sanidina C2/m K[AlSi3O8] – polimorf de T°h Si, Al – distributie dezordonata in pozitiile tetraedrice T1 si T2 K+ – ocupa spatiile largi, pe planele de simetrie mb Clivaj 

  14. FELDSPATII Feldspatii K Sanidina C2/m Ortoza (orthoclase) C2/m Microclin -1 Creste ordinea Si-Al Feldspatul Na (albitul) Monalbit (2/m) – T°> High-albit (-1) – distributie dezordonata Si-Al, T°~ Low-albit (-1) – distributie ordonata Si-Al, T°< Microclin – roci intruzive, racite lent Ortoza – r. intruzive, T intermediare Sanidina – r. efuzive, lave de T> Feldspatii plagioclazi -1 -anortitul - distributie ordonata Si-Al -str.~microclin

  15. FELDSPATII Exsolutie lame de albit intr-un cristal de feldspat K PERTITE Plagioclaz+lamele K-fd. ANTIPERTITE

  16. Exsolutia temperatura ridicata cantitatea de solutie solida dintr-o retea cristalina depinde de razele ionice ale celor doi atomi care se substitie; Doi atomi cu raze ionice foarte diferite se vor substitui in proportii limitate; temperatura scazuta Scaderea temperaturii odata cu cresterea temperaturii, substitutiile devin posibile datorita vibratiilor atomice K-fd. Feldspatii Na+K+ ~1000° (1.18 Å) (1.51 Å) miscibilitate completa albit

  17. Microcline with tartan plaid twinning, XPL

  18. FELDSPATOIZII Termeni importanti: Nefelin Na3K[Al4Si4O16] Leucit K[AlSi2O6] Sodalit Na8[Al6Si6O24]Cl2 Nosean Na8[Al6Si6O24](SO4) Haüyn (Na,Ca)4-8[Al6Si6O24](SO4,S2Cl)1-2 Cancrinit (Na,Ca)7-8[Al6Si6O24](CO3,SO4,S2Cl)1,5-2·1-5 H2O Structura si chimism Daca feldspatii reprezinta minerale saturate în silice (pot forma împreuna cu cuartul o parageneza), feldspatoizii sunt minerale subsaturate în silice. Formulele lor por fi întelese plecând de la cele ale feldspatilor corespunzatori: Na[AlSi3O8] - 2 SiO2 = Na[AlSiO4], albit nefelin K[AlSi3O8] - SiO2 = K[AlSi2O6] ortoza leucit

  19. FELDSPATOIZII nefelin leucit sodalit Na3K[Al4Si4O16] K[AlSi2O6] Na8[Al6Si6O24]Cl2 T1,T4 – Al T2,T3 - Si

  20. 0,5 mm Leucite Observations: Paramorphic replacement of high-leucite (cubic) by low leucite (tetragonal) results in twinning and crossed interfrerence patterns.

  21. NU trebuie retinute formulele

  22. ZEOLITII http://www.iza-structure.org/databases/