ZnO 纳米阵列制备及气敏特性研究 工作开展照片

ZnO 纳米阵列制备及气敏特性研究 工作开展照片. 指导老师：苏治斌 项目负责人：胡奇辉 项目成员：石晓忪 郭凯. 图 11000/4500r/min 下的 ZnO 纳米阵列的形貌. 最佳工艺（成果）. 图 22 层籽晶层的 ZnO 纳米阵列的形貌. 最佳工艺（成果）. 图 3 预处理温度 300℃ 时间为 20min 下的 ZnO 纳米阵列的形貌. 图 4 退火温度 550℃ ，退火时间为 60min 的 ZnO 纳米阵列的形貌. 最佳工艺（成果）. 图 5 生长液浓度为 0.025 mol/L 制备的 ZnO 纳米阵列的形貌.

chava
Download Presentation

ZnO 纳米阵列制备及气敏特性研究 工作开展照片

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. ZnO纳米阵列制备及气敏特性研究工作开展照片 指导老师：苏治斌 项目负责人：胡奇辉 项目成员：石晓忪 郭凯

  2. 图11000/4500r/min下的ZnO纳米阵列的形貌 最佳工艺（成果） • 图22层籽晶层的ZnO纳米阵列的形貌

  3. 最佳工艺（成果） • 图3预处理温度300℃时间为20min下的ZnO纳米阵列的形貌 • 图4退火温度550℃，退火时间为60min的ZnO纳米阵列的形貌

  4. 最佳工艺（成果） • 图5生长液浓度为0.025 mol/L制备的ZnO纳米阵列的形貌 • 图6生长时间为60min的ZnO纳米阵列的形貌

  5. 图7最佳工艺制备的制备ZnO 纳米薄膜和ZnO 纳米阵列XRD

  6. 掺杂Al ZnO纳米阵列 • 图8掺杂Al摩尔百分比为2%的ZnO纳米阵列 • 图9掺杂Al摩尔百分比为3%的ZnO纳米阵列

  7. 图10.电阻灵敏度

  8. 使用仪器 • 电子分析天平 • 甩膜机

  9. 使用仪器 • 超声波振荡器 • 箱式电阻炉

  10. 使用仪器 • 水浴锅 • 药品

  11. 相关样品

  12. 相关样品 • 气敏元件 • 陶瓷管以及薄膜制品