An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Materials selection - properties

  2. Materials selection - properties

  3. Materials selection - properties

  4. Materials selection - environment

  5. Bicycle frames

  6. Bicycle frames

  7. Bicycle frames – hot piercing for seamless tubing

  8. Bicycle frames – cold drawing of seamless tubing Cold drawing – need high formability ––> extensive work-hardening

  9. Bicycle frames

  10. Bicycle frames

  11. Bicycle frames – common materials used density modulus Plain carbon steel 7.8 gm/cc 200GPa Cr-Mo steel 7.8 200 6061–T6 2.7 70 Ti-3Al-2.5V 4.5 110 Polymer composite yield yield/density Plain carbon steel 240 MPa 30 Cr-Mo steel 485 62 6061–T6 260 95 Ti-3Al-2.5V 700 156

  12. A little bit more on Ti and its alloys Ti is polymorphic: -Ti (hcp) ––> -Ti(A2) at 882°C Ti mostly alloyed with Al, V Remember - & -Fe w/ chromium, & nickel Various elements have different solubilities in - & -Ti

  13. A little bit more on Ti and its alloys Ti-3Al-2.5V is an "- alloy" Enuf -stabilizer (V) added so that a little  phase can exist at room temp &  phase solution strengthened by Al & V  alloys are stronger than those containing only  or  phase

  14. Joining techniques Conventional arc welding Tungsten inert gas (TIG) welding Brazing Adhesive bonding

  15. Use butted tubing for strengthening HAZ region Joining techniques Plain carbon steel frame – TIG welded Tubing is strengthened by drawing operation – but softened near weld

  16. Joining techniques Cr-Mo steel frame – TIG welded But weld and HAZ harder than tubing – more rapid cooling than that experienced by tubing – get Bainite original tube