一、 压缩成型原理和过程

一、 压缩成型原理和过程. 压缩成型主要用于热固性塑料塑件的生产。与注射成型相比，其优点是可以使用普通压力机进行生产；压缩模没有浇注系统，结构比较简单；塑件内取向组织少，取向程度低性能比较均匀；成型收缩率小等。缺点是成型周期长、劳动强度大、生产环境差、生产操作多用手工而不易实现自动化；高度方向的尺寸精度不易控制；模具易磨损，因此使用寿命较短。. 一、 压缩成型原理和过程. 压缩成型原理. 压缩成型动画. 压缩成型原理图. 压缩成型压机. 一、 压缩成型原理和过程. 压缩成型设备. 二、 压注成型原理和过程. 压注成型动画. 压注成型原理.

chul
Download Presentation

一、 压缩成型原理和过程

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 一、 压缩成型原理和过程 压缩成型主要用于热固性塑料塑件的生产。与注射成型相比，其优点是可以使用普通压力机进行生产；压缩模没有浇注系统，结构比较简单；塑件内取向组织少，取向程度低性能比较均匀；成型收缩率小等。缺点是成型周期长、劳动强度大、生产环境差、生产操作多用手工而不易实现自动化；高度方向的尺寸精度不易控制；模具易磨损，因此使用寿命较短。

  2. 一、 压缩成型原理和过程 • 压缩成型原理 压缩成型动画 压缩成型原理图

  3. 压缩成型压机 一、 压缩成型原理和过程 压缩成型设备

  4. 二、 压注成型原理和过程 压注成型动画 压注成型原理 特点塑料在进入型腔前已经塑化，能生产外形复杂、薄壁或壁厚变化很大，带有精细嵌件的塑件；保压硬化时间较短，缩短了成型周期，提高了生产效率；塑件的密度和强度也得到提高；塑件精度容易保证，表面粗糙度也较低。

  5. 压注成型压机

  6. 三、成型工艺条件 1. 成型压力 压缩成型压力是指液压机对塑件在垂直于加压方向的平面上的单位投影面积所施加的作用力。

  7. 三、 成型工艺条件 2. 成型温度 压缩成型温度 压缩成型温度是指压缩成型时所需的模具温度。成型物料在模具温度作用下，必须经由玻璃态熔融成粘流态之后才能流动充模，最后还要经过交联才能固化定型为塑料制件，所以压缩过程中的模具温度对塑件成型过程和成型质量的影响，比起注射成型显得更为重要。

  8. 三、 成型工艺条件 3. 成型时间 热固性塑料压缩成型时，要在一定温度和一定压力下保持一定时间，才能使其充分地交联固化，成为物性优良的塑件，这一时间称为成型时间。

  9. 四、 塑料液压机极其选用 塑料液压机: 上压式液压机 下压式液压机 上压下压式液压机 角式液压机