1 / 7

超 宽温 稳定型介质材料 二价金属掺杂研究

超 宽温 稳定型介质材料 二价金属掺杂研究. 报告人：张 宁 导　师 ：李玲霞 教授. 研究背景. 片式多层陶瓷电容 器的广泛应用. 宽温化. 小型化. 低成本化. 研究背景. 钛酸钡基介质材料. 钛酸钡 - 钛酸铋钠基 介质材料. 超宽 温稳定型 介质材料. 铅基复合钛矿体系. 介电常数 >1500 介电损耗 <2 . 0% 电容量变化 率 <±15% 工作温度范围 -55~300 ℃ 绝缘电阻 率 > 10 12 Ω•cm 烧结温度 <1150 ℃. 钨青铜矿结构体系.

deon
Download Presentation

超 宽温 稳定型介质材料 二价金属掺杂研究

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 超宽温稳定型介质材料二价金属掺杂研究 报告人：张 宁 导　师：李玲霞 教授

  2. 研究背景 片式多层陶瓷电容器的广泛应用 宽温化 小型化 低成本化

  3. 研究背景 钛酸钡基介质材料 钛酸钡-钛酸铋钠基 介质材料 超宽温稳定型 介质材料 铅基复合钛矿体系 介电常数>1500 介电损耗<2.0% 电容量变化率<±15% 工作温度范围-55~300℃ 绝缘电阻率>1012Ω•cm 烧结温度<1150℃ 钨青铜矿结构体系

  4. BT-NBT-Nb-MO(M=Mg, Zn, Co, Ni, Mn)介质材料研究 MgO掺杂BT-NBT-Nb [0.85BT-0.15NBT]-2wt%Nb2O5- x wt% MgO X= 0.0, 0.5, 1.0, 1.5, 2.0 不同含量MgO掺杂样品的介电性能及体积密度

  5. BT-NBT-Nb-MO(M=Mg, Zn, Co, Ni, Mn)介质材料研究 不同含量MgO掺杂样品的介温曲线

  6. BT-NBT-Nb-MO(M=Mg, Zn, Co, Ni, Mn)介质材料研究 二价金属氧化物掺杂BT-NBT-Nb [0.85BT-0.15NBT]-2wt%Nb2O5- 1.5 wt% MO M=Mg, Zn, Co, Ni, Mn 不同二价金属氧化物掺杂样品的介电性能 不同二价金属氧化物掺杂样品的介温曲线

  7. 谢谢大家！