5.1 鐵碳平衡圖

5.1 鐵碳平衡圖. 5.1 鐵碳平衡圖. 波來鐵內肥粒鐵與雪明 碳鐵的量維持定值，可利用槓桿原理求得。. 5.1 鐵碳平衡圖. 碳鋼的共析組織乃是肥粒鐵與雪明碳鐵層層相疊的層狀組織，稱為波來鐵。. 5.1 鐵碳平衡圖. 5.1 鐵碳平衡圖. 5.1 鐵碳平衡圖. 5.2 恆溫變態曲線圖與連續冷卻曲線圖. — 波來鐵. — 糙斑鐵. — 吐粒散鐵. — 麻田散鐵. 5.2 恆溫變態曲線圖與連續冷卻曲線圖. 5.2 恆溫變態曲線圖與連續冷卻曲線圖. 5.2 恆溫變態曲線圖與連續冷卻曲線圖.

erik
Download Presentation

5.1 鐵碳平衡圖

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 5.1 鐵碳平衡圖

  2. 5.1 鐵碳平衡圖 • 波來鐵內肥粒鐵與雪明 碳鐵的量維持定值，可利用槓桿原理求得。

  3. 5.1 鐵碳平衡圖 • 碳鋼的共析組織乃是肥粒鐵與雪明碳鐵層層相疊的層狀組織，稱為波來鐵。

  4. 5.1 鐵碳平衡圖

  5. 5.1 鐵碳平衡圖

  6. 5.1 鐵碳平衡圖

  7. 5.2 恆溫變態曲線圖與連續冷卻曲線圖 —波來鐵 —糙斑鐵 —吐粒散鐵 —麻田散鐵

  8. 5.2 恆溫變態曲線圖與連續冷卻曲線圖

  9. 5.2 恆溫變態曲線圖與連續冷卻曲線圖

  10. 5.2 恆溫變態曲線圖與連續冷卻曲線圖 • 麻田散鐵之Ms與Mf只隨含碳量而異，與冷卻速度無關 。 • 麻田散鐵變態的量為溫度的函數，與時間無關。

  11. 5.2 恆溫變態曲線圖與連續冷卻曲線圖 • 鋼的恆溫變態

  12. 5.2 恆溫變態曲線圖與連續冷卻曲線圖

  13. 5.2 恆溫變態曲線圖與連續冷卻曲線圖 • 在TTT曲線鼻部上方 • 在低於粗波來鐵變態溫度下

  14. 5.2 恆溫變態曲線圖與連續冷卻曲線圖 • 針狀肥粒鐵中有小板狀的雪明碳鐵 • 羽毛狀肥粒鐵中有細長的雪明碳鐵

  15. 5.2 恆溫變態曲線圖與連續冷卻曲線圖

  16. 5.2 恆溫變態曲線圖與連續冷卻曲線圖

  17. 5.2 恆溫變態曲線圖與連續冷卻曲線圖 • 麻田散鐵與波來鐵之混合物

  18. 5.3 碳鋼之熱處理方法 • 淬火

  19. 5.3 碳鋼之熱處理方法

  20. 5.3 碳鋼之熱處理方法 • 含碳量愈高，冷速愈大，斷面愈小，質量效果也愈小

  21. 5.3 碳鋼之熱處理方法

  22. 5.3 碳鋼之熱處理方法 • 回火

  23. 5.3 碳鋼之熱處理方法 • 退火

  24. 5.3 碳鋼之熱處理方法 • 正常化

  25. 5.3 碳鋼之熱處理方法

  26. 5.3 碳鋼之熱處理方法

  27. 5.4 熱處理爐及其週邊設備

  28. 5.4 熱處理爐及其週邊設備

  29. 5.4 熱處理爐及其週邊設備

  30. 5.4 熱處理爐及其週邊設備