CT-7 So urces of phase - equilibrium data:

CT-7 So urces of phase - equilibrium data:. T hermal analysis, quantitative metallo - graphy, microprobe measurements, two-phase tie-lines, three-phase tie-lines, X-ray, electron and neutron diffraction. Binary phase-diagram data. Measured quantities in binary phase diagram:

forrest-hogan
Download Presentation

CT-7 So urces of phase - equilibrium data:

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. CT-7 Sources of phase-equilibrium data: Thermal analysis, quantitative metallo-graphy, microprobe measurements, two-phase tie-lines, three-phase tie-lines,X-ray, electron and neutron diffraction

  2. Binary phase-diagram data • Measuredquantities in binaryphase diagram: • Temperaturesof invariant (three-phase) equilibria • Points on theboundariesoftwo-phasefields • measuredforsamplesofknowncomposition by determining • T ofphasechange • Determiningphasecomposition (1 phaseor 2 phases) • forseriesofsamplesofdifferentcompositionannealedat T

  3. Liquid TmA liquidus solvus a+ L a b+L peritectic TmB AxBy +L b eutectic AxBy a+ AxBy AxBy +b Phase Diagrams T P = const. A xB B Schmetterer C.: 13. Austrian Chemistry Days 2009

  4. Phase Diagrams Technologically important example: Fe-Fe3C

  5. Phase Diagrams Technologically important example: Fe-Fe3C

  6. Binary phase-diagram data-cont. LFS - CT

  7. Binary phase-diagram: compositions of phases. • Rule 1 and 2: If we know T and Co, then we know: --the composition of each phase. --the amount of each phase (given in wt%) – lever rule Cu-Ni system • Examples: Adapted from Fig. 9.2(b), Callister 6e. (Fig. 9.2(b) is adapted from Phase Diagrams of Binary Nickel Alloys, P. Nash (Ed.), ASM International, Materials Park, OH, 1991.) 7 Callister W.D. Materials Science and Engineering. John Wiley 1999.

  8. Example: COOLING IN A Cu-Ni BINARY • Phase diagram: Cu-Ni system. Cu-Ni system • System is: --binary i.e., 2 components: Cu and Ni. --isomorphous i.e., complete solubility of one component in another; a phase field extends from 0 to 100wt% Ni. • Consider Co = 35wt%Ni. Adapted from Fig. 9.3, Callister 6e. 10 Compare Scheil-Gulliver solidification model Callister W.D. Materials Science and Engineering. John Wiley 1999.

  9. CORED VS. EQUILIBRIUM PHASES • Ca changes as we solidify. • Cu-Ni case: First a to solidify has Ca = 46wt%Ni. Last a to solidify has Ca = 35wt%Ni. • Fast rate of cooling: Cored structure • Slow rate of cooling: Equilibrium structure Influence of diffusion: Homological temperature Th = T / Tm 11 Callister W.D. Materials Science and Engineering. John Wiley 1999.

  10. HYPOEUTECTIC & HYPEREUTECTIC Adapted from Fig. 9.7, Callister 6e. (Fig. 9.7 adapted from Binary Phase Diagrams, 2nd ed., Vol. 3, T.B. Massalski (Editor-in-Chief), ASM International, Materials Park, OH, 1990.) (Figs. 9.12 and 9.15 from Metals Handbook, 9th ed., Vol. 9, Metallography and Microstructures, American Society for Metals, Materials Park, OH, 1985.) Adapted from Fig. 9.15, Callister 6e. Adapted from Fig. 9.15, Callister 6e. (Illustration only) Adapted from Fig. 9.12, Callister 6e. 20

  11. Thermal analysis • The sample is heated or cooled and its temperature is recorded with time. • When sample is going from a single-phase equilibrium state into a two-phase field, some heat of precipitation is released, which can be sensitively detected by the use of differential thermal analysis (DTA)

  12. DTA curves and phase diagram in Ba-Cu system LFS - CT

  13. Tammann triangle • Three-phase equilibrium (T=const.): • In thermal analysis - horizontal part of T(t) curve (eutectic dwell time) • Length of this part is proportional to matter reacting at T=const. • Plotting this length vs.mole fraction for eutectic reaction: • Tammann triangle – vertex indicates mole fraction of the eutectic liquid (Sauveur diagram) – determination of xE • In scanning calorimeter – quantitatively correctly measured. • For peritectic reaction – often segregation – use it with caution!

  14. Lazerges, M.; Rietveld, I.; Corvis, Y.; et al. THERMOCHIMICA ACTA   497  (1-2)   124-128   (2010)

  15. Thermal analysis-cont. Sensitivity of thermal analysis is larger for flat two-phase field boundary than for steep two-phase field boundaries

  16. Properties vs. temperature Thermal analysis: singularity on H(T) curve is used to identify boundaries between different fields of phase diagram Other property can be used for this purpose: Length of sample (T) – dilatometry Electric conductivity (T) – resistometry Magnetic susceptibility (T) - magnetometry

  17. Properties vs. composition Isothermal annealing of many samples: Lattice parameter (xi) – X-ray diffraction (it is constant in two-phase field and varies in single-phase field) Electrical conductivity (xi) - resistometry

  18. Metallography Optical microscope Objective Objective Different orientation of grains Transmission mode Reflection mode

  19. Metallography-cont. Much of information from metallography is qualitative (single-phase field / two-phase field). Boundaries between single-phase and two-phase fields are mapped by hand. (In binary- as well as in ternary- systems.) LFS - CT

  20. Metallography-cont. Quantitative metallography: In the micrograph of two-phase sample the ratio of areas covered by images of two phases can be measured representing the volume ratio of two phases. If molar molumes of two phases are known, molar ratio can be calculated from volume ratio. Grinding and polishing errors should be taken into account.

  21. Quantitative metallography Image analysis Blackparticles – sigma-phase a b c Figuresweretakenafterannealingat 700 oCfor a) 500 hrs, b) 3000 hrs, c) 6000 hrs. Kraus M., Kroupa A., Miodownik P., Svoboda M., Vrestal J.: Int.J.for Mat. Res., accepted

  22. Microprobe measurements Electron gun Anode Lenses Condensors Screen Screen

  23. Microprobe measurements-cont. In the electron microprobe, areas of the order of 1 m2 can be chemically analyzed by X-ray spectroscopy (in spite of that the electron beam can be focused to d=50 nm). (ZAF – corrections, standards or standard-less methods) (EDX or WDX analysis) In two-phase samples annealed long enough for they to have large grains enough and being in equilibrium – equilibrium composition of both phases can directly be analyzed (tie-lines).

  24. Ternary miscibility gap Overall composition of two-phase sample analyzed have to be on the determined tie-line. (K.J.Laidler et.al.: Physical Chemistry, 4.ed., Houghton Mifflin Co., Boston, p.253 )

  25. Ternary phase-diagram data Methods used to localize boundaries in ternary system – in principle the same as for binary ones. Two independent variables for composition description – two different types of measurements of mole fraction for the same phase

  26. T C Binary system AC Binary system BC vertical cut: Isoplethal Section C horizontal cut: Isothermal Section A B Binary system AB A B The Ternary Phase Diagram P=const. Schmetterer C.: 13. Austrian Chemistry Days 2009

  27. Thermal analysis in ternary system The temperature of primary crystallisation and the temperature of an invariant equilibrium are found in the same manner as in a binary system. Tammann triangle – pyramid with two independent composition variables (e.g. mole fractions). Between primary crystallization and invariant equilibrium, the secondary crystallisation may begin with an additional kink in DTA-line.

  28. Two-phase tie-lines Similarly as in the binaries, either the temperature may be measured, where this boundary is at the given composition or, the composition may be measured where this boundary is found at a given temperature.

  29. Two-phase tie-lines-cont. T = const. Error of experiment: LFS - CT

  30. Directions of two-phase tie-lines Tie-lines connects composition points where the chemical potentials i are the same in both phases. Calculated values of these chemical potentials, however, are given by the description of the previously optimized binary systems. Such a measurements are, therefore, a check of the compatibility of the two binary descriptions.

  31. Directions of two-phase tie-lines-cont. LFS - CT

  32. Ternary three-phase equilibria The experimental methods are the same as for isothermal two-phase equilibria. Lattice parameters are constant within a three-phase field. Amounts of phases in equilibrium can be measured by quantitative metallography.

  33. Ternary three-phase equilibria Example: In-Sb-Sn ternary system – 100 oC and 300 oC Calculation: binary prediction (only binary data used) Experiment: Solubility of In in SbSn phase determined and used for improvement of calculations Ternary three-phase tie-lines check the binary prediction (note saving of experimental work) Manasijevic D. et.al.: Journal of Alloys and Compounds 450 (2008) 193-199

  34. Multicomponent experimental data Usually not directly used in assessment – Used as check of extrapolation from the lower-order system (e.g. binary prediction of ternary system) – modification of parameters describing the lower-order systems.

  35. Example : Phase diagram Cr-Mo Cr-Mo system: Fcc phase is not stable in a binary system – Parameters for CALPHAD method for it are necessary – have to be assessed from the higher-order system. Possible influence of performed modifications on lower-order systems must be checked carrefully.

  36. X-ray and neutron diffraction Determination of crystal structures in single-crystalline samples. Lattice parameters and site occupancies as functions of compositions and temperature can be obtained. (Different scattering factors of X-rays and neutrons: complementary information.) Ordering can be observed (see example)

  37. X-ray and neutron diffraction-example LFS - CT

  38. Rietveld refinement Determination of site-occupancy parameters by analyzing intensity ratios of X-ray- or neutron-diffraction spectra of polycrystalline samples.

  39. Mössbauer spectroscopy Recoil-free resonance absorbtion of -rays Measure of local state of ordering and site occupancy (namely Fe and Sn systems - „ Mössbauer“ nuclei Fe57 and Sn119) (Magnetic moment on the nucleus is sensitive to the local surroundings of it.)

  40. Other experimental data related to phase equilibrium Theoretical and experimental data not directly used in assessments but important: Phonon spectra – for excess term of Gibbs energy (vibrational contribution to the entropy) Elastic constants, bulk modulus, thermal expansion – for derivatives of Gibbs energy

  41. Questions for learning • 1. What information concerning of phase diagram we can receive using optical metallography? • 2. What information concerning of phase diagram we can receive using differential thermal analysis or differential scanning calorimetry? • 3. What information concerning of phase diagram we can receive using dilatometry, resistometry, magnetometry? • 4. What information concerning of phase diagram we can receive using scannning electron microscopy (with EDX analyser), X-ray diffractometry? • 5. What information concerning of phase diagram we can receive using Rietveld refinement and Mössbauer spectroscopy?