激光固态相变与激光熔凝

Φ720mm. 激光固态相变与激光熔凝. 展板二. 采用功率密度为 10 4 ~10 5 W/cm 2 的激光束，在金属表面扫描： 将表层迅速加热到奥氏体转变温度以上，熔点以下，通过工件自身导 热，快速冷却实现细小马氏体的转变 —— 激光固态相变硬化（激光 淬火）。 将表层迅速加热到熔化，随后快速冷却凝固，得到细微的组织 —— 激 光快速熔凝。. 特点

garrett-stewart
Download Presentation

激光固态相变与激光熔凝

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Φ720mm 激光固态相变与激光熔凝 展板二 • 采用功率密度为104~105 W/cm2的激光束，在金属表面扫描： • 将表层迅速加热到奥氏体转变温度以上，熔点以下，通过工件自身导 • 热，快速冷却实现细小马氏体的转变——激光固态相变硬化（激光 • 淬火）。 • 将表层迅速加热到熔化，随后快速冷却凝固，得到细微的组织——激 • 光快速熔凝。 特点 加热和冷却的速度极快，组织大大细化均匀，硬度比传统热处理高，可大幅度提高工件的耐磨性、疲劳强度、耐腐蚀能力。 过程精确可控，适于对工件局部进行处理，无污染，工件变形很小，处理后只需少量磨削加工或可不加工。 应用范围 适用于灰铸铁、球墨铸铁、中碳钢、中碳合金钢、工具钢、模具钢、马氏体不锈钢等制作的各种零件的局部硬化处理。如曲轴、齿轮、气缸套、活塞环槽、冲盘、模具等表面硬化。 齿轮齿面激光淬火 制药机械零部件激光熔凝强化(替代进口) 长2.5米，直径50～60mm细长空心轴表面激光淬火，挠曲变形仅0.06～0.15mm 挤管模具内表面激光熔凝强化 曲轴激光淬火 联系方式： 地址:天津市塘沽区新港三号路4号 邮编：300456 天津修船技术研究所 激光加工研究室 Tel：022-25795642 Fax：022-25794559 E－mail：6313laser@sina.com

More Related