An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Principle of the process Structure Process modeling Defects Design For Manufacturing (DFM) Process variation Metal forming Rolling Module 8

  2. Rolling Process: Mechanics Analysis • Two opposite rolls and a piece of material flows between them. The shape of rolls can be designed in a different form to construct a product with different cross sections. handout 8 b

  3. System parameters Operating parameters Objectives of mechanics analysis • Physical phenomenon • Torque • Power • Productivity handout 8 b

  4. w t L Physical phenomenon Spreading: Volume before rolling = the volume after rolling Volume flow rate conservation handout 8 b

  5. Vo < Vr < Vf No-slip point Slipping Slipping Work velocity = Roll velocity handout 8 b

  6. For the rolling process, the true strain is: The average flow stress is the same expression, i.e. e n k = Y f + 1 n handout 8 b

  7. It is the friction between the work and the roll that drives the workflow between two rolls. Greater Friction Force Lesser Friction Force No-slip point • The friction force is developed based on • coefficient of the friction and • compression force of rolls handout 8 b

  8. Max. Possible Draft Radius of the roll Friction coefficient Friction causes Rolling If Friction=0, then draft=0, means NO ROLLING Condition to roll- Coefficient of the friction draft, d = |tf-t0|: dmax handout 8 b

  9. Condition to roll- Power to drive the roll and work piece Roll Force (F) Integrating “unit roll pressure” over roll work “contact area” The pressure varies along the contact length handout 8 b

  10. Torque Contact length d Contact force N: rotation speed of the roll, rev / min Power Power is a function of D. Increase of D leads to increase of P handout 8 b

  11. Condition to roll- Power to drive the roll and work piece When the required power (d) is greater than the supplied power, the rolling of a work piece with d is not possible. Therefore, the required power = supplied power will lead to a critical draft d or maximum d. Criterion 1: Criterion 2: required power = supplied power  The actual maximum draft for a rolling system is the smaller one computed from the two criterions above.

  12. Example: A 10-in. –wide, 1.0-in – thick plate is to be reduced in a single pass in a two-high rolling mill to a thickness of 0.8 in. The roll has a radius = 20 in., and its speed = 50 ft/min. The work material has a strength coefficient = 35.000 lb/in.2 and a strain hardening exponent = 0.2. Determine (a) roll force, (b) roll torque, and (c) power required to accomplish this operation. handout 8 b

  13. Given: rolling, t0=1.0 in., tf=0.80 in., w=10.0 in., R=20 in., vr=50 ft/min, flow curve n=0.20 and K=35,000 lb/in2. Find: (a) F, (b) T, (c) HP. Draft d=1.0-0.8=0.2 in. Contact length L = (20×0.20)0.5 = 2.0 in. True strain ε = ln (1.0/0.8) = ln 1.25= 0.223 Average flow stress f = 35,000(0.223)0.20/1.20 = 21,607 lb/in2 Rolling force F = 21,607(10)(2) = 423,149 lb handout 8 b

  14. Torque T = 0.5(432,149)(2.0) = 432,149 in-lb. N = (50 ft/min)/(2π×20/12) = 4.77 rev/min. Power P=2 π (4.77)(432,149)(2) = 25,929,940 in-lb/min HP = (25,929,940 in-lb/min)/(396,000) = 65.5 hp handout 8 b