Density Functional Theory of Iron Carbide and Steel Surface Erosion Chemistry

Density Functional Theory of Iron Carbide and Steel Surface Erosion Chemistry. Wun C. Chiou, Jr Emily A. Carter University of California, Los Angeles Dept. of Chemistry & Biochemistry. Thanks: Funding : U. S. Army Research Office

jontae
Download Presentation

Density Functional Theory of Iron Carbide and Steel Surface Erosion Chemistry

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Density Functional Theoryof Iron Carbide andSteel Surface Erosion Chemistry Wun C. Chiou, Jr Emily A. Carter University of California, Los Angeles Dept. of Chemistry & Biochemistry Thanks: Funding: U. S. Army Research Office Resources: Maui High Performance Computing Facility, Army Research Laboratory MSRC

  2. - Steel Erosion Issues - Problem: In a harsh operating environment, an exposed steel surface can erode, leading to decreased performance, safety concerns, and repair/replacement costs. • Petrochemical Industry Processes • Steam Reformers • Gun Tubes • Industrial Furnaces • CO2-cooled Nuclear Reactors • Coal Gasification Processes Environment: Impact: T ~ 1700 K High Pressures Chemicals (H2, O2, CO, CO2, NO, NO2, and etc) Mechanical Forces

  3. - Carburization - Definition: A high-temperature corrosion phenomenon caused by carbon ingress from the environment into metal components, leading to internal carbide precipitation and changes to the mechanical properties of the materials. Grabke, H. J. Carburization: A High Temperature Corrosion Phenomenon. MTI, 1998. Mechanism: • C/CO transport to the steel surface • C diffuses into the surface • Solid state reaction with Fe in steel • Fem + CnÞ FemCn Consequences: • Phase-change stresses • Altered ductile properties, grain cohesion • MP-lowering: TM~1800K Þ TM<1500K • Metal Dusting: disintegration of the steel in a dust of metal particles and C

  4. DFT Results - Bulk Fe3C - Similar to bulk Fe (mostly d-state contributions near EF) Integrated DOS shows some charge transfer from Fe to C: Cementite charge/atom: C: 4.5 Fe: 7.3 (bcc-Fe: 5.267) Geometry-optimized cementite properties

  5. - Surfaces of Fe3C - Investigate the relative stability of low-index surfaces of Fe3C, cementite. Narrowed search to four surfaces: stoichiometric, high density, and minimal dangling bonds from the cut (100), (001), (110), (011) Results: unrelaxed surfaces Esurf = (Eslab - N*Ebulk) / 2A Esurf (J/m2): (110) 2.37 (001) 2.40 (011) 2.56 (100) 2.72

  6. - Surfaces of Fe3C - Relative stability correlates with surface smoothness: Surface Es,unr(J/m2) (100) 2.72 (011) 2.56 (001) 2.40 (110) 2.37

  7. - Surfaces of Fe3C - Relaxations into the surfaces: (100) relaxed (100) (001) (001) relaxed Face Surface energy Relaxation rms (J/m2) energy (%) relaxation (Å) Static Relaxed (100) 2.72 2.47 10 % 0.012 (011) 2.58 2.55 1 % 0.007 (001) 2.40 2.05 15 % 0.016 (110) 2.37 2.34 1 % 0.013

  8. - Conclusion - Iron carbide and carburization are important aspects of steel erosion Bulk Ecoh improves on earlier predictions Cementite DOS is similar to pure Fe, but with some charge transfer to C Surface stability: (001) > (110) > (011) > (100) Fe3C/Fe Interface calculations Carbide formation