Measurement of Water Vapour Permeation: Current State of the Art and Future Challenges. “We invent and build permeation measurement equipment”. Holger Nörenberg, Technolox Ltd. , Oxford, UK www.technolox.com. Problem: How to ensure a sufficiently long lifetime

Download Presentation

Holger Nörenberg, Technolox Ltd. , Oxford, UK technolox

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Measurement of Water Vapour Permeation: Current State of the Art and Future Challenges “We invent and build permeation measurement equipment” Holger Nörenberg, Technolox Ltd. , Oxford, UK www.technolox.com

  2. Problem:How to ensure a sufficiently long lifetime of flexible electronics to make money • Key Aspect:Failure due to ingress of water vapour • Solution:Barrier layer to prevent ingress of water vapour • Good Barrier?Measurement of the permeation of WV • Problem 1:Very small amount of water vapour to be measured • Problem 2: Short Measurement time, easy operation

  3. Current State of the Art Solubility S & Diffusion D = Fickian Diffusion: P=D·S Permeation P

  4. Applications of Barrier Layers • Flexible OLED displays • Lighting • Photovoltaics • E-paper • Thin-film devices (batteries,…)

  5. Measurement of 10-4 … 10-6 g/m2/day: We are getting there • Calcium Test • Tritium Test • MOCON Aquatran • Technolox Deltaperm

  6. www.vitexsys.com Optical Calcium Test • Observation of the corrosion of a thin calcium layer • Position-resolved information • Parallel processing

  7. Electrical Calcium Test • Monitoring conductance and 1/f noise during Ca-degradation • Sensitivity <10-6 g/m2/day • www.imre.a-star.edu.sg

  8. Tritium Test • Sensitivity 10-6 g/m2/day • www.ga.com

  9. MOCON Aquatran • Detection limit: 5x10-4 g/m2/day • www.mocon.com H2O in Carrier gas (N2) Coulometric sensor

  10. Total Pressure Method valve upstream side Water vapour upstream side Water vapour 2: Admission of water vapour to the upstream side. pump OFF sample Pump ON sample pressure sensor downstream side downstream side PC 3: Measuring the total pressure p(t) means of a pressure sensor. upstream side Water vapour Pump OFF sample pressure sensor downstream side p t 1: Evacuation of upstream side and downstream to remove the ambient air • Sensitivity: <2x10-4 g/m2/day • suitable for gases and vapours • wide parameter range (100oC)

  11. Raw Data • Information Contents: Rate of Permeation ~ Slope of Dp=f(t)

  12. Inorganic barrier • on 100mm PEN- • substrate 10-4g/m2/day and below 40oC • Information Contents: WVTR=f(T) “Activation Energy” • Can be (carefully) used for interpolation or extrapolation (“accelerated testing”

  13. Deltaperm Sensitivity • @5x10-5 g/m2/day low noise level • Challenge: reduce or understand background signal

  14. Challenges • Sensitivity • Sample conditioning - Measurement time • Distinguishing between good barriers caused by a long time-lag or by low permeability • Parameter range of measurement (temperature, RH): valuable tool • Interpretation of “unwanted effects” (background signal, noise, edge permeation, outgasing, …) • Easy operation • Theoretical understanding of the permeation process

  15. Sensitivity: How small is 10-6g/m2/day? • 10-6 x 0.1 x 3652 = 3.7x10-4g WV • fits into a water droplet of Ø 0.9 mm • Typical substrate: 100 mm thick polyester (PET, PEN) S=0.005gWV/gPET 3x10-3 gWV/m2 (RH=50%) 10-6 g/m2/day

  16. Sample Conditioning A B C D Both sides of sample under ambient conditions Upstream side exposed to water vapour (RH=0.9) Downstream side of sample under vacuum

  17. Single Barrier • Sample can initially take up water

  18. Multilayers • WVTR may fall first • and increase later

  19. WV through PEN @23ºC Time-lag • Information Contents: Rate of Permeation, Diffusion Coefficient, Solubility

  20. S= Some Theory • Transient conditions: D = L2/6tlag • Stationary conditions: P = const • • This algorithm works for ideal gases and homogeneous materials • Multilayers: system of differential equations

  21. Outgasing of WV Uptake of WV time

  22. Outgasing: Water Vapour leaves the Sample US PET or PEN DS • Water vapour leaves the • sample (outgasing) • After some WV has accumulated • outside the sample it is removed • with a vacuum pump • More WV leaves the sample • WV removed again • And so on • Pressure increase due to outgasing • is summed up and the total amount • of WV coming from the sample • is then calculated

  23. Water Vapour enters the Sample PET or PEN • A dry sample is exposed to water • vapour • Sample takes up WV • More WV is admitted • Sample takes up more WV • And so on • The pressure decrease of the • WV is summed up and used to • calculate the amount of WV that • has gone into the sample

  24. Conclusions • Various methods method suitable to measure WVTR in the 10-4 … 10-6 g/m2/day-range • Wealth of information from permeation measurement • Measurement under stationary and transient conditions • Valuable tools: T, RH • Outgasing • Theoretical calculations should complement experimental work • A lot of challenges remain !!! Thank you very much for your attention!