1 / 17

固体氧化物燃料电池及电解质材料研究

固体氧化物燃料电池及电解质材料研究. 张红鹃. 燃料电池的研究背景. 不同碳酸盐含量的氧化铈基电解质比较. Pr 2 NiO 4 -Ag 复合阴极在 SOFC 中的应用. 优势： 高效率、环境友好、燃料灵活. 3. 4. 不同碳酸盐含量的氧化铈基电解质研究. Zhu B. 等提议的 DCO- 碳酸盐复合材料界面导电示意图. 共沉淀法. (Li/Na) 2 CO 3. 混合. 热处理. LNSDC. Ce 3+ , Sm 3 + 溶液. 680 o C 40 min. 混合. 干燥. 煅烧. 抽滤. 搅拌. 悬浮液. SDC.

kay-robinson
Download Presentation

固体氧化物燃料电池及电解质材料研究

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 固体氧化物燃料电池及电解质材料研究 张红鹃

  2. 燃料电池的研究背景 不同碳酸盐含量的氧化铈基电解质比较 Pr2NiO4-Ag复合阴极在SOFC中的应用

  3. 优势： • 高效率、环境友好、燃料灵活 3

  4. 4

  5. 不同碳酸盐含量的氧化铈基电解质研究 Zhu B.等提议的DCO-碳酸盐复合材料界面导电示意图

  6. 共沉淀法 (Li/Na)2CO3 混合 热处理 LNSDC Ce3+, Sm3+溶液 680 oC 40 min 混合 干燥 煅烧 抽滤 搅拌 悬浮液 SDC 100 oC 600oC 2 h 草酸 阻抗测试 压片Ag/LNSDC/Ag 恒压测试 致密度测试

  7. 待做 电化学性能测试 H2氛围下阻抗与电导率测试 LiAlO2-LNSDC/ LNSDC/ NiO-LNSDC Ag/LNSDC/Ag

  8. Pr2NiO4-Ag复合阴极在SOFC中的应用 • 制备：共沉降+浸渍法

  9. 制备方法的优化 Ag添加量的优化

  10. 谢谢！