1 / 22

Quantum Dots – a peep in to Synthesis Routes

Quantum Dots – a peep in to Synthesis Routes. Saurabh Madaan Graduate student, Materials Science and Engineering, University of Pennsylvania. Layout. Brief introduction Synthesis routes – an overview. First Vision of Quantum Dot device.

kenley
Download Presentation

Quantum Dots – a peep in to Synthesis Routes

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Quantum Dots – a peep in to Synthesis Routes Saurabh Madaan Graduate student, Materials Science and Engineering, University of Pennsylvania

  2. Layout • Brief introduction • Synthesis routes – an overview

  3. First Vision of Quantum Dot device Arakawa, Sakaki… > Efroz, Brus >Bawendi & Alivisatos…

  4. Quantum Dots – an Introduction • Confined 3-D structures – bohr-exciton radius is less than material dimensions (5.6 nm for CdSe) • Unique electronic, optical properties ~ particle in a box

  5. Nanocrystals, Artificial Atoms • Blue shift; tunable spectra • High quantum efficiency • Good candidates for biological tagging, sensing applications

  6. Synthesis Routes TOP-DOWN • Lithography (Wet-chemical etching, E-field) BOTTOM-UP • Epitaxy (self assembly or patterned; S-K or ALE) • Colloidal chemistry routes • Templating (focused ion beam, holographic lithography, direct writing)

  7. Lithography/ Etching

  8. Lithography/ Electric Field • Quantum well > quantum wire > quantum dot : by etching • Confinement: growth direction – qwell; lateral directions – electrostatic potential

  9. Lithography Route – Limitations • Edge effects • Defects due to reactive ion etching • Less control over size • Low quantum efficiency • Slow, less density, and prone to contamination

  10. MBE – Self-assembled NCs • Initial stage – InAs (7% mismatch) grows layer-by-layer 2D mechanism. • Strained layer – wetting layer • When amount of InAs exceeds critical coverage (misfit > 1.8% ), 3D islands are formed • Stranski-Krastanow 3D growth

  11. MBE: Vertical Coupling in S-K growth PHYSICAL REVIEW B 54 (12): 8743-8750 SEP 15 1996

  12. MBE Self-assembled NCs: 2 modes

  13. MBE Self-assembled NCs: 2 modes

  14. MBE Self-assembled NCs: Features - No edge effects, perfect Xtal structure - Qdot lasers, single photon generation, detection - Annealing leads to blue shift • Undesired fluctuations in size and density – broadened spectra • Random distribution on lateral surface area – lack of positioning control • Cost!

  15. Monodisperse NCs – Colloidal Route • La Mer and Dinegar – discrete nucleation followed by slow growth • uniform size distribution, determined by time of growth • Ostwald Ripening in some systems Murray, Kagan, Bawendi

  16. Solution-phase Route (continued) • high-T supersaturation • or • 2. low-T supersaturation • When rate of: injection < consumption, no new nuclei form Fig: a) synthesize NCs by high T solution-phase route, b) narrow size dist by size selective ppt, c) deposit NC dispersions that self-assemble, d) form ordered NC assemblies (superlattices).

  17. Colloidal Route – Compounds 1. Nucleation and Growth: 2. Isolation and purification:anyhdrous methanol > flocculate > drying 3. Size-selective precipitation: solvent/non-solvent pairs eg. Pyridine/hexane

  18. Further Treatments More steric hinderance? Layer of high band-gap SC, higher quantum efficiency

  19. Colloidal Route – Controlling size • Time growth, Ostwald ripening • Temperature growth, O. r. • Reagent/Stabilizer concentration more nucleation, small size • Surfactant chemistryprovide capping layer. So, more binding, more steric effect, small size • Reagent additionrate of injection<feedstock addition… “focus” the size-distribution • When desired size is reached (absorption spectra), further growth is arrested by cooling (15-115 angstrom range possible) • Possible problems: • Inhomogeneity in injection of precursors • Mixing of reactants • Temperature gradients in flask

  20. Mass-limited Growth in Templates

  21. Finally… Colors from the Bawendi Lab @ MIT http://www.youtube.com/watch?v=MLJJkztIWfg