An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Semiconducting -FeSi2 Presented by Srujana Aramalla

  2. Silicides • Metallic Silicides e.g. CoSi2, NiSi2, TiSi2 • Semiconducting silicides e.g. b-FeSi2 (bandgap of 0.85 eV), CrSi2 (0.35 eV)and ReSi2 (0.12 eV).

  3. Advantages of Transition metal silicides • Temperature stability • Oxidation resistance • Low electrical resistivity

  4. FeSi2-Phases Exists in two phases • Semiconducting low temperature  phase • Metallic high temperature  phase -FeSi2 - FeSi2 ~937C

  5. Bandgap of -FeSi2 Quasi direct bandgap ~0.83 eV - ~0.87 eV (at RT)

  6. Nature of bandgap

  7. Optical characterization • Raman spectroscopy -provides information related to structure and bonding

  8. Samples investigated • -FeSi2 (undoped) • -(Fe(1-X)Crx)Si2 (x=0.003, 0.01) • -(Fe(1-X)Cox)Si2 (x=0.009, 0.066, 0.14)

  9. Growth method Molecular beam epitaxy The deposition can consist of 1.Pure metal deposition at room temp, followed by annealing (SPE) 2.pure metal deposition at high temp (RDE) 3.codeposition of metal and silicon

  10. Raman Spectroscopy Specifications: • 0.85m Double monochromator equipped with a pair of 1200 grooves/mm holographic gratings • 5145 Ar ion laser as excitation source with output power at 300 mW • Photo multiplier detector tube.

  11. Information obtainable from Raman spectrum • Raman intensity • The frequency shift • The linewidth

  12. Results

  13. Results

  14. Conclusion • Observed overall red shift if the peaks is related to tensile stress in the samples. • Tensile stress observed in these samples may result in sufficient strain to cause Y-point transition to become the fundamental direct transition, thus allowing light emission.

  15. Thank You…