高透光高隔熱奈米隔熱噴劑 MESM01GC01/02 產品說明書

高透光高隔熱奈米隔熱噴劑 MESM01GC01/02 產品說明書. 米特奈米科技股份有限公司 http://www.m-9.com.tw. UV. VIS. IR. 氧化鎢. Multi layer sputtering. Plastic forming. LaB6 coating. ATO coating. 本產品 (MESM01GC01/02) 與其他產品的比較. Compare with other products. 特點 (MESM02S). 高透光 , 高隔熱 簡易噴塗 , 有自乾型及熱固化型 兩種

lila-oconnor
Download Presentation

高透光高隔熱奈米隔熱噴劑 MESM01GC01/02 產品說明書

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 高透光高隔熱奈米隔熱噴劑MESM01GC01/02產品說明書高透光高隔熱奈米隔熱噴劑MESM01GC01/02產品說明書 米特奈米科技股份有限公司 http://www.m-9.com.tw

  2. UV VIS IR 氧化鎢 Multi layer sputtering Plastic forming LaB6 coating ATO coating 本產品 (MESM01GC01/02) 與其他產品的比較 Compare with other products 特點(MESM02S) • 高透光, 高隔熱 • 簡易噴塗,有自乾型及熱固化型 兩種 • 與同等級之濺鍍膜相比,價格便宜 • 添加氧化鎢,不易褪色 • 不會干擾無線電通訊 IR Cut film

  3. MESM01GC01/02的規格. • 高透光高隔熱奈米隔熱噴劑 MESM01GC01/02: • (1)使用無機奈米氧化鎢粒子.不易褪色. • (2)塗層不會有藍暈現象( bluish haze). • (3)MESM01GC01屬自乾型,噴塗24小時後會建立硬度,48小時後 • 始可碰觸. • (4)MESM01GC02屬熱固化型,硬化時間為180℃,30分鐘. • (5)玻璃噴塗前需經清潔處理. • (6)可依需要,控制噴塗的厚度.噴塗量越多,抗IR抗UV效果越好. • (7)內含物:溶劑,樹脂,助劑,奈米氧化鎢粒子等. • (8)自乾型(MESM01GC01),建議以噴霧瓶或空壓噴槍噴塗. • (9)熱固化型(MESM01GC02),建議以超音波噴塗設備噴塗.

  4. 三種塗佈樣品的全光譜穿透圖 TOP1:一層塗佈 TOP2:二層塗佈 TOP3:三層塗佈 噴塗量越多,抗IR效果越顯著.

  5. 玻璃噴塗前後光學數據比較 玻璃噴塗前 VLT:81% IRC:81% 噴塗後:VLT:73%,IRC:91%

  6. MESM01GC01/02塗膜的加速老化試驗(QUV) 由上圖結果顯示,塗膜經紫外燈(340nm)照射500小時後, 僅發生極少的變化.幾乎不會褪色. (塗層必須添加UV吸收劑)