新型肽基复合水凝胶制备

新型肽基复合水凝胶制备. 赵君. Content . 1. Fmoc -FF/ 海藻酸钠复合水凝胶微球 2. Fmoc -FF/ 聚丙烯酰胺复合纳米膜. 1. Fmoc -FF/ 海藻酸钠复合水凝胶微球. 1 ）不同混合方式 ①用 DMSO 溶解的 Fmoc -FF 与海藻酸钠溶液混合 ②用碱性 Fmoc -FF 溶液与海藻酸钠溶液混合后加酸中和. 1 分钟. 2 分钟. 5 分钟. DMSO 溶解混合. 1. Fmoc -FF/ 海藻酸钠复合水凝胶微球. 1 分钟. 碱性 Fmoc -FF 溶液混合.

ling
Download Presentation

新型肽基复合水凝胶制备

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 新型肽基复合水凝胶制备 赵君

  2. Content • 1. Fmoc-FF/海藻酸钠复合水凝胶微球 • 2. Fmoc-FF/聚丙烯酰胺复合纳米膜

  3. 1. Fmoc-FF/海藻酸钠复合水凝胶微球 1）不同混合方式 ①用DMSO溶解的Fmoc-FF与海藻酸钠溶液混合 ②用碱性Fmoc-FF溶液与海藻酸钠溶液混合后加酸中和 1分钟 2分钟 5分钟 DMSO溶解混合

  4. 1. Fmoc-FF/海藻酸钠复合水凝胶微球 1分钟 碱性Fmoc-FF溶液混合 加酸后出现白色絮状物，2分钟后无法用注射器取出样品，可能已经出现块儿状凝胶。

  5. 1. Fmoc-FF/海藻酸钠复合水凝胶微球 2）不同的成胶环境 ①混合溶液滴至混有HCl的CaCl2溶液中 ②混合溶液直接滴至CaCl2溶液中 滴入加有HCl的CaCl2溶液中 凝胶材料混合比较均匀，成胶过程同步性较高，但是在溶液中成型困难，不能组装成宏观可见的光滑微球表面。

  6. 1. Fmoc-FF/海藻酸钠复合水凝胶微球 直接滴加至CaCl2溶液中 材料表面不均一，可能是成胶过程不同步造成的，但是在宏观成球的过程速度很快，而且表面光滑。

  7. 1. Fmoc-FF/海藻酸钠复合水凝胶微球 3）对比实验 ①海藻酸钠溶液在CaCl2溶液中成球 ②Fmoc-FF溶液在CaCl2溶液中成球 Magnification=50000 海藻酸钠成球

  8. 1. Fmoc-FF/海藻酸钠复合水凝胶微球 Fmoc-FF成球

  9. 1. Fmoc-FF/海藻酸钠复合水凝胶微球 4）凝胶实验 先加Ca2+后加H+ 先加H+后加Ca2+ H+可以减慢海藻酸钠的成胶速率，从而使胶体的微观结构更均一。

  10. 2. Fmoc-FF/聚丙烯酰胺复合纳米膜 单晶Si表面成膜内外层结构

  11. 2. Fmoc-FF/聚丙烯酰胺复合纳米膜 玻璃片上不同位置的膜表面

  12. 2. Fmoc-FF/聚丙烯酰胺复合纳米膜 膜厚大约1μm

  13. 谢谢！