An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Progress on coatings and grooves • M.Taborelli • Progress on C based coatings • Progress on SEY instrument • Progress on grooves

  2. Progress on coatings Effect of the sputtering gas used during carbon film deposition: Ne and Kr Lowest yield up to now

  3. Progress on coatings measured at CERN after 2h air after 14 d air Complete yield curve (measured at CSIC-Madrid) After 2 weeks air exposure dep. with Kr Dep. with Ne

  4. Progress on coatings C(Kr), in SPS now Both coatings are quite Compact and well adhering C(Ne)

  5. Progress on coatings • The reason of the lower SEY is not understood yet • Implanted gas? some of the Kr deposited coating show Kr in the spectra (original reason for the Ne trial!) • No difference in the C1s XPS spectra • No difference in the content of O • difference in morphology, xtalline structure……? C(Kr) C1s XPS C(Ne)

  6. Plans for next coatings (….find candidate for next liner) - reproduce a C(Ne) coating and its SEY - make rough surface (Cu or Zr) as substrate for low SEY (C) coating - BC with lower amount of B (B4C has a rather high yield, already measured) - SiC, TiB2

  7. Progress on SEY instrument First data from new system: unbaked copper

  8. Progress on SEY instrument • Still to be optimized, verified…built: • - Control of focussing (at present some 2 mm spot, but not • well controlled above 1000eV) • Position (distance) with respect to “optics” • Beam position stability at low Ep and magnetic field screening • Load lock and transfer to XPS still under construction • SPS transfer chamber under construction (J.Axensalva and J.Ramillon) • Phase II: • Faster acquisition to avoid high dose...however it seems to be already OK • Implement flood gun for conditioning with e-beam

  9. Progress on grooves Grooves made at CERN workshop with cutting tool (J.M.Geisser, S.Atieh) 2mm On copper: tool well aligned, small radii on top and bottom, but burrs along the grooves On stainless steel 304L: Preliminary trial without perfect alignment of the tool: large radius at the bottom

  10. Progress on grooves Grooves in copper

  11. Progress on grooves To continue the work: Cost of what has been done until now (short piece on steel and copper): 2000 CHF work + 2000 CHF tool = 4000 CHF To produce 800 mm x 100 mm (or 400 mm + 400 mm) on steel: 2000 CHF tools + 4000 CHF work =6000 CHF If we go on the entire amount will be charged: 10000 CHF