1 / 15

XRD analysis report

XRD analysis report. Prepared for: Los Alamos National Lab Prepared by: Aya Takase (aya.takase@rigaku.com) November 11, 2010. Contents. Sample list 3 MPA (Eulerian cradle) 4 Analysis requests 5 Additional analyses 6 Phase ID and peak selection 7

malaya
Download Presentation

XRD analysis report

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. XRD analysis report Prepared for: Los Alamos National Lab Prepared by: Aya Takase (aya.takase@rigaku.com) November 11, 2010

  2. Contents • Sample list 3 • MPA (Eulerian cradle) 4 • Analysis requests 5 • Additional analyses 6 • Phase ID and peak selection 7 • Nb pole figures 8 – 9 • Cu pole figures 10 – 12 • Nb texture analysis 13 • Cu texture analysis 14 • Summary 15

  3. Sample list

  4. MPA (Eulerian cradle) Rotating angle: φ (β) Measurement range: -360 – 360 °, 0.005 ° step Tilt angle: χ (α, ψ) Measurement range: -5 – 92 °, 0.002 ° step Sample height axis: Z (-4 – 1 mm, 0.0005 mm step)

  5. Requested analyses • Cu/Nb multilayer on Si • Pole figures of Cu (111) and Nb (110)

  6. Additional analyses • Cu/Nb multilayer on Si • Pole figures of Cu (200), (220) and Nb (200)

  7. Cu/Nb / phase ID & peak selection Parallel beam Ultima IV / Standard Parallel beam Att.: MPA Detector: SC XG: 40 kv – 44 mA DS: 1 x 5 mm Soller S.: 5 º PSA: 0.5 º Mono: None Axis:θ/ 2θ scan Range: 30.0 – 80.0 º Step: 0.1º Speed: 1.0 º / min RD sample Si(004)

  8. CuNb / Nb(110) pole figure Parallel beam Ultima IV / Standard Parallel beam Att.: MPA Detector: SC XG: 40 kv – 44 mA DS: 1 x 2 mm Soller S.: 5 º PSA: 0.5 º Mono: None 2θ = 38.900 º, fixed α: 15 – 90 º, 5 º step β: 0 – 390 º, 5 º step β speed: 120 º / min Duration: 54 min

  9. CuNb / Nb(200) pole figure Parallel beam Ultima IV / Standard Parallel beam Att.: MPA Detector: SC XG: 40 kv – 44 mA DS: 1 x 2 mm Soller S.: 5 º PSA: 0.5 º Mono: None 2θ = 55.800 º, fixed α: 15 – 90 º, 5 º step β: 0 – 390 º, 5 º step β speed: 30 º / min Duration: 206 min

  10. CuNb / Cu(111) pole figure Parallel beam Ultima IV / Standard Parallel beam Att.: MPA Detector: SC XG: 40 kv – 44 mA DS: 1 x 2 mm Soller S.: 5 º PSA: 0.5 º Mono: None 2θ = 43.542 º, fixed α: 15 – 90 º, 5 º step β: 0 – 390 º, 5 º step β speed: 240 º / min Duration: 30 min

  11. CuNb / Cu(200) pole figure Parallel beam Ultima IV / Standard Parallel beam Att.: MPA Detector: SC XG: 40 kv – 44 mA DS: 1 x 2 mm Soller S.: 5 º PSA: 0.5 º Mono: None 2θ = 50.484 º, fixed α: 15 – 90 º, 5 º step β: 0 – 390 º, 5 º step β speed: 60 º / min Duration: 103 min

  12. CuNb / Cu(220) pole figure Parallel beam Ultima IV / Standard Parallel beam Att.: MPA Detector: SC XG: 40 kv – 44 mA DS: 1 x 2 mm Soller S.: 5 º PSA: 0.5 º Mono: None 2θ = 74.321 º, fixed α: 15 – 90 º, 5 º step β: 0 – 390 º, 5 º step β speed: 30 º / min Duration: 206 min

  13. Nb texture analysis Major orientation = ♦ [110] fiber texture, minor orientation = ■ [100] fiber texture 0º Nb (110) 60º 60º 45º 45º 45º 45º Nb (200) 0º * Intensity in square root scale

  14. Cu texture analysis Major orientation = ▲ [111] fiber texture, minor orientation = ■ [100] fiber texture 0º Cu (111) 55º 55º 70º 70º 0º Cu (200) 55º 55º 35º 35º Cu (220) 45º 45º * Intensity in square root scale

  15. Summary • Nb(110), (200), Cu(111), (200), and (220) pole figures were collected. • Nb layers have strong [110] fiber texture and relatively weak [100] fiber texture. • Cu layers have strong [111] fiber texture and relatively weak [100] fiber texture.

More Related