摘自高立圖書陳文照等編著「材料科學與工程導論」第 304 頁. 【 補充 】 鐵－碳化鐵（ Fe-Fe 3 C ）相圖. 圖 AA-1 是鐵－碳相圖的一部分。當加熱時，純鐵在熔化之前經歷兩次結晶構造的改變。室溫下純鐵的穩定形態稱為 肥粒鐵 （ ferrite ）或 α 鐵，具有 BCC 結晶構造。肥粒鐵在 912℃ 經歷一同素異形相變態成為 FCC 結構的 沃斯田鐵 （ austenite ）或 γ 鐵。 沃斯田鐵一直保持到 1394℃ ，再由 FCC 結構的 沃斯田鐵 再轉變回 BCC 結構的  肥粒 鐵。 純鐵最後於 1538℃ 熔化成液相。.

miriam-stone
Download Presentation

摘自高立圖書陳文照等編著「材料科學與工程導論」第 304 頁

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 摘自高立圖書陳文照等編著「材料科學與工程導論」第304頁摘自高立圖書陳文照等編著「材料科學與工程導論」第304頁

  2. 【補充】鐵－碳化鐵（Fe-Fe3C）相圖 • 圖 AA-1 是鐵－碳相圖的一部分。當加熱時，純鐵在熔化之前經歷兩次結晶構造的改變。室溫下純鐵的穩定形態稱為肥粒鐵（ferrite）或 α 鐵，具有 BCC 結晶構造。肥粒鐵在 912℃經歷一同素異形相變態成為 FCC 結構的沃斯田鐵（austenite）或 γ鐵。 • 沃斯田鐵一直保持到1394℃，再由FCC 結構的沃斯田鐵再轉變回BCC結構的  肥粒鐵。 • 純鐵最後於1538℃熔化成液相。

  3. 【補充】鐵－碳化鐵（Fe-Fe3C）相圖 • 圖 10.28 中的成分軸只達到 6.70 wt% C，在這個濃度形成中間化合物碳化鐵或雪明碳鐵（cementite；Fe3C），在相圖上它是以一條垂直線表示。 • 在BCC結構α 鐵中只能溶解極少濃度的碳，最大溶解度是在727℃下的0.022wt%。 • 碳在沃斯田鐵中最大溶解度為2.14wt%，發生在1147℃。

  4. 【補充】鐵－碳化鐵（Fe-Fe3C）相圖 • 共析反應：沃斯田鐵變態成波來鐵（肥粒鐵加雪明碳鐵）（727℃，含碳量0.76%） • 共晶反應：液相變態成沃斯田鐵加上雪明碳鐵（1147℃，含碳量4.3%） • 包晶反應：液相加肥粒鐵變態成沃斯田鐵（1493℃，含碳量0.17%） • 亞共析鋼、共析鋼（0.76%C）、過共析鋼 • 亞共晶鑄鐵、共晶鑄鐵、過共晶鑄鐵 • 低碳鋼(0.25以下)、中碳鋼、高碳鋼(0.6~1.4)

  5. 【補充】鐵－碳化鐵（Fe-Fe3C）相圖 • 0.45%C的碳鋼是屬於哪一種鋼？（1）中碳鋼；（2）共析鋼；（3）亞共析鋼；（4）低碳鋼。 • 答：（1）and（3） • 0.45%C的碳鋼在750℃時具有何種顯微組織？ • 答：肥粒鐵and沃斯田鐵 • 0.45%C的碳鋼在700℃時具有何種顯微組織？ • 答：初析肥粒鐵and波來鐵