8.3光在各向异性介质中的传播. 8.3.1双折射 一、双折射的概念 由于折射率与原子紧密堆积有关，所以对于各向异性材料，在不同的方向上表现出不同的折射率值，因此，当光束通过各向异性介质的表面时，由于在各方向上的折射程度不同，折射光会分成两束沿着不同的方向传播。这种现象称为双折射。 二、双折射现象产生的机理 用介质的极化理论解释双折射现象 用光波和物质相互作用理论解释双折射现象.

ori-bridges
Download Presentation

8.3光在各向异性介质中的传播

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 8.3光在各向异性介质中的传播 8.3.1双折射 一、双折射的概念 由于折射率与原子紧密堆积有关，所以对于各向异性材料，在不同的方向上表现出不同的折射率值，因此，当光束通过各向异性介质的表面时，由于在各方向上的折射程度不同，折射光会分成两束沿着不同的方向传播。这种现象称为双折射。 二、双折射现象产生的机理 用介质的极化理论解释双折射现象 用光波和物质相互作用理论解释双折射现象

  2. 三、电控双折射效应 ：一束光线与细晶透明铁电陶瓷斜交并沿此方向传播时，会产生双折射，即光线被分解为两束线偏振光。这种双折射率可借助于外加电场的变化或陶瓷剩余极化强度的变化来进行控制，这便是电控双折射效应。

  3. 8.3.2旋光 一、概念 在某一单轴晶体内沿着垂直于光轴方向切出一块平行平面晶片，并将其插入一对正交偏振片之间，在单色光的照射下，从偏振片II后看去视场变亮。此时如把偏振片II向左或向右旋转一定的角度，出现消光现象。 这表明，从晶片透射出来的光仍为线偏振光，但其振动面向左或向右旋转了一个角度，这种现象称为旋光。

  4. 二 、旋光的机理 三、法拉第旋转效应 （1）对于给定的介质，振动面的转角与样品的长度l和磁感应强度B成正比：=FLB 式中，F为法拉第旋转系数（（）/cm）。 （2）光的传播方向反转时，法拉第旋转的左右方向互换。