Inorganic UV Filters

1. Perspectives on Supplying Attenuation Grades of Titanium Dioxide and Zinc Oxide for Sunscreen ApplicationsDavid Schlossman, Yun Shao, Ph.D., Pascal Delrieu, Ph.D., Kobo Products Inc.

2. Titanium dioxide (TiO2) and zinc oxide (ZnO) pigments are commonly used in personal care products to provide protection against UVA and UV B They attenuate UV light by absorption and scattering They are usually surface coated to minimize photo-catalytic activity. They are typically produced as finer crystals from the same feed stocks and with similar processes as pigmentary grades. Inorganic UV Filters

3. The production of TiO2 and ZnO is a two step process : 1. Purification of the raw material 2. Growing of crystals (primary particles) of the desired size They are two different processes for TiO2, known as sulfate and chloride, and three for ZnO, known as American, French and Wet. Crystals are grown at high temperatures to the required sizes : 200 nm and above (pigmentary grades) and finer than 200 nm (attenuation grades). Manufacturing Process Attenuation grades Pigmentary grades 10nm 200nm

4. M. Kobayashi and al., Cosm & Toil., Vol. 112, No. 6, p83, 1997 * Rate constant of the first order reaction of oxydation of acetalydehyde It is common industry practice to use surface treated inorganic UV filters when formulating sunscreens. Surface Treatment Surface Treatment of Inorganic UV Filters

5. Attenuation of UV light is influenced by particle size. Scattering of visible light (whitening effect) is influenced by particle size and the difference between the refractive index of the pigment and the surrounding media. Maximum scattering occurs when size equals 1/2 the wavelength and particles are uniformly dispersed (Mie theory). Optical Properties - TiO2 and ZnO Absorption TiO2 : 420 nm (rutile) / 390 nm (anatase) ZnO : 380 nm (3.24 eV) Scattering Refractive Index : TiO2: 2.76 ( Rutile) / 2.52 (Anatase) ZnO: 1.99 Wavelength Particle size

6. Particle Size and Light Scattering Typical existing form supplied >1 mm UV Visible Size reduction Whitening Transparent

7. Dispersions of Attenuation Grade TiO2 Comparison of Dispersions and Powders 15 nm TiO2 35 nm TiO2 Dispersion vs Powder Dispersion vs Powder *Freeze Fracture TEM (40,000X) Smaller primary particles are more difficult to disperse : 11/1 ratio of dispersion size to primary particle size for 10 nm TiO2).

8. 10nm TiO2 (110 nm dispersion particle size) makes transparent dispersions for all skin types. All dispersions diluted in Cyclopentasiloxane (to 20% TiO2) TiO2 Dispersions in Cyclopentasiloxane 195 60 35 15 10 nm 195 60 35 15 10 nm 195 60 35 15 10 nm 195 60 35 15 10 nm

9. 308/360 extinction ratio : indication of UVB/UVA balance 308/524 extinction ratio : indication of transparency Particle Size and UV attenuation

10. Effect of Particle Size on Attenuation Inorganic Sunscreen Formulations * Tests were performed by Consumer Product Testing Co. - All testing on 3 people ** FDA method *** JCIA PPD method (Rating 2-4: +; 4 - 8: ++; 8 - 12: +++).

11. Attenuation grade Titanium Dioxide and Zinc Oxide are produced using the same processes as larger pigmentary grades. They are usually surface coated to minimize their photo-catalytic activity. TiO2 and ZnO attenuate UV light according to their particle size : Small primary particle sizes (10 - 15 nm) are necessary to produce dispersions (100 - 150 nm) transparent to visible light and efficient against UVB. ZnO and larger TiO2 (35 - 150 nm) are more efficient against UVA. The particle size of pigmentary grades are appropriate to scatter visible light, but they are not efficient at attenuating UV light or effective as sunscreens. Conclusions