FIB-STEM Observation Report of LES Cathode camera 2

Analysis of LES cathode camera 2 surface using Matlab script, identifying subsets and observations of disordered regions and superficial layer effects. No visible dislocation structure observed.

rmegan
Download Presentation

FIB-STEM Observation Report of LES Cathode camera 2

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. FIB-STEM Observation Report of LES Cathode camera 2 EN Division-Materials and Metrology CERN/EN/MME-MM/EDMS XXXXXXX

  2. Introduction: • The set of LES “camera 2” was analysis on EDMS n. 1752821 Automatic counting = 489 Manual counting = 504

  3. Observation: • N. Pienimaki develop a Matlab script to divide surface in elements and 3 subsets:

  4. Observation:

  5. Reference

  6. Reference Reference

  7. 1 BD observation 1 BD observation

  8. 1 BD observation 1 BD observation

  9. 2 BD observation

  10. 2 BD observation

  11. Summary of observations • No dislocation structure visible. • Superficial layer affected on reference region (plastic deformation during machining?). • Disordered on 1 BD and 2 BD