General Concepts Chapter 2

General Concepts Chapter 2. Professor Joe Greene CSU, CHICO. MFGT 144. Chapter 2 Objectives. Objectives Monomers and Polymerization Homopolymers Amorphous State Crystallinity Cross-linking and Molecular Networks Copolymers Polyalloys Fillers, Reinforcements Additives. Bonding. e-.

sadie
Download Presentation

General Concepts Chapter 2

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. General ConceptsChapter 2 Professor Joe Greene CSU, CHICO MFGT 144

  2. Chapter 2 Objectives • Objectives • Monomers and Polymerization • Homopolymers • Amorphous State • Crystallinity • Cross-linking and Molecular Networks • Copolymers • Polyalloys • Fillers, Reinforcements • Additives

  3. Bonding e- e- e- e- H H H H H C C e- e- e- e- e- e- e- e- e- e- H H e- H • Covalent bonding (most important for plastics) • Occurs when two nonmetal atoms are in close proximity. • Both atoms have a tendency to accept electrons, which results in shared outer electron shells of the two atoms. • Number of shared electrons is usually to satisfy the octet rule. • Resulting structure is substantially different that the individual atoms, e.g., C and H4 make CH4, a new and distinct molecule. • Atoms is covalent bonds are not ions since the electrons are shared rather than transferred as in ionic or metallic bonds. e-

  4. Bonding • Secondary bonding: weaker than ionic, metallic, covalent • Hydrogen bonding • Occurs between the positive end of a bond and the negative end of another bond. • Example, water the positive end is the H and the negative end is O. • van der Waals • Occurs due to the attraction of all molecules have for each other, e.g. gravitational. Forces are weak since masses are small • induced dipole • Occurs when one end of a polar bond approaches a non-polar portion of another molecule.

  5. Naming Organic Compounds • Basis for naming organic compounds • Indicate the family of organic compounds to which a molecule belongs (importance to polymers) • Dependent upon functional group, e.g. alcohol group, methanol or methyl alcohol. • Dependent upon the number of carbon atoms in the repeating molecule. Number Counting Carbons Counting functional groups • 1 C Meth mono • 2 C Eth Di • 3 C Pro Tri • 4 C But Tetra • 5 C Pent Penta • Example, • CH4 has one carbon and no functional groups (alkane), thus is meth ‘ane. • C2H2 has 2 carbons and has a double bond (alkene), thus is eth ‘ene.

  6. Monomers and Polymerization H H H H H H Polyethylene polymer (powder or solid) H H C C C C C C C C …... H H H H H H H H • Polymers are formed from a • monomer, which is a small (low MW) molecules with inherent capability of forming • chemical bonds with the same or other monomers in such a manner that long chains (polymer chains or macromolecules) are formed • Typical polymer chains involves hundreds or thousands of monomeric molecules Ethylene Monomer (gas) Polymerization …... Heat, pressure, catalyst

  7. Definition of Plastics • Plastics come from the Greek plastikos, which means to form or mold. • Plastics are solids that flow (as liquid, molden, or soften state) when heat is applied to material. • Polymers are organic materials that come from repeating molecules or macromolecules • Polymer materials are made up of “many” (poly) repeating “units”(mers). • Polymers are mostly based in carbon, oxygen, and hydrogen. Some have Si, F, Cl, S • Polymers are considered a bowl of spaghetti or a bag of worms in constant motion.

  8. Polymerization Mechanisms • Chain Growth (Addition) Polymerization • Polymerization begins at one location on the monomer by an initiator • Instantaneously, the polymer chain forms with no by-products • Step-wise (Condensation) Polymerization • Monomers combine to form blocks 2 units long • 2 unit blocks form 4, which intern form 8 and son on until the process is terminated. • Results in by-products (CO2, H2O, Acetic acid, HCl etc.)

  9. Condensation Polymerization Example • Polyamides • Condensation Polymerization • Nylon 6/6 because both the acid and amine contain 6 carbon atoms NH2(CH2)6NH2 + COOH(CH2)4COOH Hexamethylene diamene Adipic acid n[NH2(CH2)6NH2 ·CO(CH2)4COOH] (heat) Nylon salt [NH(CH2)4NH·CO(CH2)4CO]n + nH2O Nylon 6,6 polymer chain

  10. Polymerization Methods • 4 Methods to produce polymers • Some polymers have been produced by all four methods • PE, PP and PVC are can be produced by several of these methods • The choice of method depends upon the final polymer form, the intrinsic polymer arrangement (isotactic, atactic, etc), and the yield and throughput of the polymer desired. • Bulk Polymerization • Solution Polymerization • Suspension Polymerization • Emulsion Polymerization

  11. Formation of Polymers H H H H H H H H H H C C C C C C C C C C H H H Cl CH3 H H H H n n n n n • Polymers from Addition reaction • LDPE HDPE PP • PVC PS

  12. Other Addition Polymers O O O O C n • Polyetheretherketone (PEEK) • Wholly aromatic structure • Highly crystalline • High temperature resistance

  13. Other Addition Polymers O O O S S S Cl Cl CH2 CH2 • Polyphenylene • Polyphenylene oxide • Poly(phenylene sulfide) • Polymonochloroparaxylyene

  14. Other Addition Polymers H H H Y C C C C H H X X H H H Cl C C C H Cl H Cl H H C C H OCOCH3 • Vinyl- Large group of addition polymers with the formula: • Radicals (X,Y) may be attached to this repeating vinyl group as side groups to form several related polymers. • Polyvinyls • Polyvinyl chloride • Polyvinyl dichloride (polyvinylidene chloride) • Polyvinyl Acetate (PVAc) or C

  15. Formation of Polymers • Condensation Polymerization • Step-growth polymerization proceeds by several steps which result in by-products. • Step-wise (Condensation) Polymerization • Monomers combine to form blocks 2 units long • 2 unit blocks form 4, which intern form 8 and son on until the process is terminated. • Results in by-products (CO2, H2O, Acetic acid, HCl etc.)

  16. Common Polymer Synthesis • Polyamides • Condensation Polymerization • Nylon 6/6 because both the acid and amine contain 6 carbon atoms NH2(CH2)6NH2 + COOH(CH2)4COOH Hexamethylene diamene Adipic acid n[NH2(CH2)6NH2 ·CO(CH2)4COOH] (heat) Nylon salt [NH(CH2)4NH·CO(CH2)4CO]n + nH2O Nylon 6,6 polymer chain

  17. Nylon Family • The repeating -CONH- (amide) link is present in a series of linear, thermoplastic Nylons • Nylon 6- Polycaprolactam: • [NH(CH2)5CO]x • Nylon 6,6- Polyhexamethyleneadipamide: • [NH(CH2)6NHCO (CH2)4CO]x • Nylon 12- Poly(12-aminododecanoic acid) • [NH(CH2)11CO]x

  18. Polycarbonate O CH3 CH2 C CH2 OH Phenol + Acetone Bisphenol-A + water OH OH C 2 CH2 • Polycarbonates are linear, amorphous polyesters because they contain esters of carbonic acid and an aromatic bisphenol (C6H5OH) • Polymerized with condensation reaction + H2O +

  19. Polycarbonate nCOCl2 + CH2 O CH2 Bisphenol-A + Phosgene Polycarbonate + salt OH OH C C O O C CH2 CH2 n + NaCl

  20. Condensation Polymerization O O • Polyhydroxyethers (Phenoxy)- Reaction of Bisphenol A and epichlorohydrin. Similar to polycarbonate. Sold as thermoplastic epoxide resins. H H H CH2 C C C C H OH H CH2 n

  21. Other Condensation Polymers O O O O R C R C O O R C R C • Thermoplastic Polyesters • Saturated polyesters (Dacron). • Linear polymers with high MW and no crosslinking. • Polyethylene Terephthalate (PET). Controlled crystallinity. • Polybutylene Terephthalate (PBT). • Aromatic polyesters (Mylar)

  22. Other Condensation Polymers O SO2 • Polysulfones- Repeating unit is benzene rings joined by sulfone groups (SO2), an isopropylidene group (CH3CH3C), and an ether linkage (O). CH3 O C CH3 n

  23. Characteristics of Addition and Condensation • Table 2.4

  24. Polymerization by other than Addition or Condensation • Ring opening • Epoxy is created via ring opening to generate active species and initiate polymerization. • Epoxy plus amine produces epoxy polymerization • Nylon 6 is formed when caprolactam ring is opened. • Acetal polymer is made by the opening of the trioxane ring.

  25. Polymer Length • Polymer notation represents the repeating group • Example, -[A]-DP where A is the repeating monomer and DP represents the number of repeating units. • Molecular Weight • Way to measure the average chain length of the polymer • Defined as sum of the atomic weights of each of the atoms in the molecule. • Example, • Water (H2O) is 2 H (1g) and one O (16g) = 2*(1) + 1*(16)= 18g/mole • Methane CH4 is 1 C (12g) and 4 H (1g)= 1*(12) + 4 *(1) = 16g/mole • Polyethylene -(C2H4)-1000 = 2 C (12g) + 4H (1g) = 28g/mole * 1000 = 28,000 g/mole =MW • Polystyrene -(C2H3)(C6H5) 1000 = 8C (12g) +8H(1g) = 104 g/mole *1000 Then MW = 104,000 = DP x M1 = 1000 * 104 = 104,000

  26. Molecular Weight • Average Molecular Weight • Polymers are made up of many molecular weights or a distribution of chain lengths. • The polymer is comprised of a bag of worms of the same repeating unit, ethylene (C2H4) with different lengths; some longer than others. • Polyethylene -(C2H4)-1000 has some chains (worms) with 1001 repeating ethylene units, some with 1010 ethylene units, some with 999 repeating units, and some with 990 repeating units. • The average number of repeating units or chain length is 1000 repeating ethylene units for a MW of 28*1000 or 28,000 g/mole .

  27. Molecular Weight • Average Molecular Weight • Distribution of values is useful statistical way to characterize polymers. • For example, • Value could be the heights of students in a room. • Distribution is determined by counting the number of students in the class of each height. • The distribution can be visualized by plotting the number of students on the x-axis and the various heights on the y-axis.

  28. Molecular Weight • Molecular Weight Distribution • Count the number of molecules of each molecular weight • The molecular weights are counted in values or groups that have similar lengths, e.g., between 100,000 and 110,000 • For example, • Group the heights of students between 65 and 70 inches in one group, 70 to 75 inches in another group, 75 and 80 inches in another group. • The groups are on the x-axis and the frequency on the y-axis. • The counting cells are rectangles with the width the spread of the cells and the height is the frequency or number of molecules • Figure 3.1 • A curve is drawn representing the overall shape of the plot by connecting the tops of each of the cells at their midpoints. • The curve is called the MolecularWeight Distribution (MWD)

  29. Molecular Weight • Average Molecular Weight • Determined by summing the weights of all of the chains and then dividing by the total number of chains. • Average molecular weight is an important method of characterizing polymers. • 3 ways to represent Average molecular weight • Number average molecular weight • Weight average molecular weight • Z-average molecular weight

  30. Gel Permeation Chromatography • GPC Used to measure Molecular Weights • form of size-exclusion chromatography • smallest molecules pass through bead pores, resulting in a relatively long flow path • largest molecules flow around beads, resulting in a relatively short flow path • chromatogram obtained shows intensity vs. elution volume • correct pore sizes and solvent critical

  31. Gel Permeation Chromatography

  32. Number Average Molecular Weight, Mn • where Mi is the molecular weight of that species (on the x-axis) • where Ni is the number of molecules of a particular molecular species I (on the y-axis). • Number Average Molecular Weight gives the same weight to all polymer lengths, long and short. • Example, What is the molecular weight of a polymer sample in which the polymers molecules are divided into 5 categories. • GroupFrequency • 50,000 1 • 100,000 4 • 200,000 5 • 500,000 3 • 700,000 1

  33. Molecular Weight • Number Average Molecular Weight. Figure 3.2 • The data yields a nonsymmetrical curve (common) • The curve is skewed with a tail towards the high MW • The Mn is determined experimentally by analyzing the number of end groups (which permit the determination of the number of chains) • The number of repeating units, n, can be found by the ratio of the Mn and the molecualr weight of the repeating unit, M1, for example for polyethylene, M1 = 28 g/mole • The number of repeating units, n, is often called the degree of polymerization, DP. • DP relates the amount of monomer that has been converted to polymer.

  34. Weight Average Molecular Weight, Mw • Weight Average Molecular Weight, Mw • Favors large molecules versus small ones • Useful for understanding polymer properties that relate to the weight of the polymer, e.g., penetration through a membrane or light scattering. • Example, • Same data as before would give a higher value for the Molecular Weight. Or, Mw = 420,000 g/mole

  35. Z- Average Molecular Weight • Emphasizes large molecules even more than Mw • Useful for some calculations involving mechanical properties. • Method uses a centrifuge to separate the polymer • Example Calculations • Mn and Mw and Polydispersity = Mw/Mn

  36. Molecular Weight Distribution • Molecular Weight Distribution represents the frequency of the polymer lengths • The frequency can be Narrow or Broad, Fig 2.3 • Narrow distribution represents polymers of about the same length. • Broad distribution represents polymers with varying lengths • MW distribution is controlled by the conditions during polymerization • MW distributions can be symmetrical or skewed.

  37. Physical and Mechanical Property Implications of MW and MWD • Higher MW increases • Tensile Strength, impact toughness, creep resistance, and melting temperature. • Due to entanglement, which is wrapping of polymer chains around each other. • Higher MW implies higher entanglement which yields higher mechanical properties. • Entanglement results in similar forces as secondary or hydrogen bonding, which require lower energy to break than crosslinks.

  38. Physical and Mechanical Property Implications of MW and MWD • Higher MW increases tensile strength • Resistance to an applied load pulling in opposite directions • Tension forces cause the polymers to align and reduce the number of entanglements. If the polymer has many entanglements, the force would be greater. • Broader MW Distribution decreases tensile strength • Broad MW distribution represents polymer with many shorter molecules which are not as entangled and slide easily. • Higher MW increases impact strength • Impact toughness or impact strength are increased with longer polymer chains because the energy is transmitted down chain. • Broader MW Distribution decreases impact strength • Shorter chains do not transmit as much energy during impact

  39. Thermal Property Implications of MW & MWD • Higher MW increases Melting Point • Melting point is a measure of the amount of energy necessary to have molecules slide freely past one another. • If the polymer has many entanglements, the energy required would be greater. • Low molecular weights reduce melting point and increase ease of processing. • Broader MW Distribution decreases Melting Point • Broad MW distribution represents polymer with many shorter molecules which are not as entangled and melt sooner. • Broad MW distribution yields an easier processed polymer Melting Point Mechanical Properties * Decomposition MW MW

  40. Melt Index • Melt index test measure the ease of flow for material • Procedure • Heat cylinder to desired temperature (melt temp) • Add plastic pellets to cylinder and pack with rod • Add test weight or mass to end of rod (5kg) • Wait for plastic extrudate to flow at constant rate • Start stop watch (10 minute duration) • Record amount of resin flowing on pan during time limit • Repeat as necessary at different temperatures and weights

  41. Melt Index and Viscosity • Melt index is similar to viscosity • Viscosity is a measure of the materials resistance to flow. • Viscosity is measured at several temperatures and shear rates • Melt index is measured at one temperature and one weight. • High melt index = high flow = low viscosity • Low melt index = slow flow = high viscosity • Example, (flow in 10 minutes) PolymerTempMass • HDPE 190C 10kg • Nylon 235C 1.0kg • PS 200C 5.0Kg

  42. Melt Index and Molecular Weight • Melt index is related closely with average molecular weight • High melt index = high flow = small chain lengths = low Mn • Low melt index = slow flow = long chain lengths = high Mn • Table 3.1 Melt Index and Average Molecular Weight MnMelt Index* (g/10min) • 100,000 10.00 • 150,000 0.30 • 250,000 0.05 * Note: PS at T= 200C and mass= 5.0Kg

  43. States of Thermoplastic Polymers • Amorphous- Molecular structure is incapable of forming regular order (crystallizing) with molecules or portions of molecules regularly stacked in crystal-like fashion. • A - morphous (with-out shape) • Molecular arrangement is randomly twisted, kinked, and coiled

  44. Amorphous Materials • PVC Amorphous • PS Amorphous • Acrylics Amorphous • ABS Amorphous • Polycarbonate Amorphous • Phenoxy Amorphous • PPO Amorphous • SAN Amorphous • Polyacrylates Amorphous

  45. States of Thermoplastic Polymers • Crystalline- Molecular structure forms regular order (crystals) with molecules or portions of molecules regularly stacked in crystal-like fashion. • Very high crystallinity is rarely achieved in bulk polymers • Most crystalline polymers are semi-crystalline because regions are crystalline and regions are amorphous • Molecular arrangement is arranged in a ordered state

  46. Crystalline Materials • LDPE Crystalline • HDPE Crystalline • PP Crystalline • PET Crystalline • PBT Crystalline • Polyamides Crystalline • PMO Crystalline • PEEK Crystalline • PPS Crystalline • PTFE Crystalline • LCP (Kevlar) Crystalline

  47. Factors Affecting Crystallinity Course Fine • Crystallization is time-dependent process • Several factors affect the speed at which it takes place (kinetics), but also the resulting morphology which can occur as course or fine grains. (Fig 2.10) • Density increases with increased crystallinity • Factors • Cooling Rate from mold temperatures • Barrel temperatures • Injection Pressures • Drawing rate and fiber spinning: Manufacturing of thermoplastic fibers causes Crystallinity • Application of tensile stress for crystallization of rubber Density Semi-cryst Amorphous Crystalline Crystallinity

  48. Form of Polymers Melt Temp Tm Rubbery Increasing Temp Tg Glassy Polymer Form • Thermoplastic Material: A material that is solid, that possesses significant elasticity at room temperature and turns into a viscous liquid-like material at some higher temperature. The process is reversible • Polymer Form as a function of temperature • Glassy: Solid-like form, rigid, and hard • Rubbery: Soft solid form, flexible, and elastic • Melt: Liquid-like form, fluid, elastic

  49. Glass Transition Temperature, Tg • Glass Transition Temperature, Tg: The temperature by which: • Below the temperature the material is in animmobile(rigid) configuration • Above the temperature the material is in a mobile (flexible) configuration • Transition is called “Glass Transition” because the properties below it are similar to ordinary glass. • Transition range is not one temperature but a range over a relatively narrow range (10 degrees). Tg is not precisely measured, but is a very important characteristic. • Tg applies to all polymers (amorphous, crystalline, rubbers, thermosets, fibers, etc.)

  50. Glass Transition Temperature, Tg Amorphous Modulus (Pa) or (psi) Crystalline Tg Tg Tg -50C 50C 100C 150C 200C 250C -50C 50C 100C 150C 200C 250C Temperature Temperature • Glass Transition Temperature, Tg: Defined as • the temperature wherein a significant the loss of modulus (or stiffness) occurs • the temperature at which significant loss of volume occurs Vol.