MIOX ® Innovative Minerals

MIOX ® Innovative Minerals. June 2009. MIOX ® as Functional Filler for Polymers. Basic properties: High Aspect Ratio Narrow particle size distribution Stable chemical properties Excellent Optic, Haptic, Organoleptic Physiologically harmless. MIOX ® Basic Properties.

shea
Download Presentation

MIOX ® Innovative Minerals

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. MIOX®Innovative Minerals June 2009

  2. MIOX® as Functional Filler for Polymers Basic properties: • High Aspect Ratio • Narrow particle size distribution • Stable chemical properties • Excellent Optic, Haptic, Organoleptic • Physiologically harmless

  3. MIOX® Basic Properties Mineralogy: Hematite, Specularite Chem. formula: Fe2O3 (iron-III-oxide) Colour: dark grey to reddish brown, metallic Shape: platy Density: 4,8 g/cm³ Hardness: 6,0–6,5 Mohs

  4. MIOX® - Unique Mineral Filler Mineralogical properties of micaceous iron oxide up to now made it impossible to keep high aspect ratio at particle sizes below 50 µm. • With our new grinding technology KMI has managed to micronize and submicronize micaceous iron oxide with high aspect ratio. • Depending on the MIOX® grade extremely high aspect ratio of more than 50:1 can be realized.

  5. MIOX® - Unique Mineral Filler Our grinding process is especially designed for the basic properties of micaceous iron oxide. • Comminution by high velocity differences guaranties high delamination combined with less mechanical deformation. • Depending on production parameters special tailor-made functional fillers for polymers can be realized. • MIOX® offers outstanding performance and an up till now never realized combination of properties in standard thermoplastics.

  6. MIOX® MICRO

  7. MIOX® MICRO and SUBMICRO

  8. MIOX® MICRO and SUBMICRO Polymer – Compounds • MIOX® MICRO und MIOX®SUBMICRO as Performance Additive for Polymers: • Melt Flow Rate MFR • E-Modulus • Impact Strength • Scratch Resistance • UV-, VIS- and IR- Absorption • Thermal Conductivity • Oxygen Permeability • Sound Absorption

  9. MIOX® MICRO and SUBMICROMFR - Melt Flow Rate & MVR – Melt Volume Rate

  10. MIOX® MICROPerformance vs. Particle Size

  11. MIOX® MICROPerformance vs. Particle Size

  12. MIOX® MICRO 20Tensile Strength & Flexural Strength vs. Particle Size IOX® in Polypropylene

  13. MIOX® vs. mineral FillersE-Modulus and Impact Strength vs. Filler Type

  14. MIOX® MICRO 10/50 Tensile Strength & Flexural Strength vs. Filler Content

  15. MIOX® MICRO 15 Tensile Strength & Flexural Strength vs. Filler Content

  16. MIOX® Surface HardnessScratch Resistance acc. Erichsen, PP-Compound

  17. MIOX® IR-VIS-UV Spectra MIOX® Filler content 30 % in 300 µm Polypropylene film

  18. MIOX® IR-Absorption PP/Talc PP/MIOX® Micro 15 MIOX® Filler content 30 % in 300 µm Polypropylene film

  19. MIOX® MICRO 20 Thermal Conductivity in Polypropylene (TC) (23°C)

  20. MIOX® Mineral Fillers Already at low filler loading significant increase of thermal conductivity is reached! As a consequence cycle time can be optimized and processing speed increases! MIOX® fillers increase productivity !

  21. MIOX® Oxygen PermeabilityO2 Permeability (air) MIOX® in 300 µm Polypropylene film

  22. Sound Absorption of Fibers Filled with MIOX® SUBMICRO Independent institutes confirmed an improvement of sound absorption up to 50% with MIOX ® SUBMICRO 2.5as active filler ! Test results based on comparative analyses of fibers tested within frequency range 100Hz up to 2.000 Hz, unfilled and with MIOX® SUBMICRO 2.5 as active filler.

  23. Improvement of Sound Absorption Fibers filled with MIOX® SUBMICRO

  24. MIOX® Application matrix

  25. MIOX® MICRO 10/50 – MICRO 20 Applications Metallic effect Sound absorption – sound damping Increase thermal conductivity IR-VIS-UV absorption

  26. MIOX® MICRO 20 – SUBMICRO 2.5 Applications Red pigment Reinforcement of mechanical properties Scratch resistance IR-VIS-UV absorption Increase thermal conductivity Sound absorption – sound damping

  27. Contact: Kärntner Montanindustrie Schloss 1 A-9400 Wolfsberg, AUSTRIA Tel: +43 (4352) 54 5 35 - 0 Fax: +43 (4352) 54 5 35 – 35 www.kmi.at Polymer Christian Rupp Director Marketing & Sales Polymer Tel. +43 (4352) 54 5 35 – 39 Mobile: +43 (664) 840 95 35 ch.rupp@kmi.at Supplied By:Kish Company 8020 Tyler Blvd. #100. Mentor, OH 44060 Phone:(440) 205-9970 Fax:(440) 205-9975 Email: Info@kishcompany.com