Ceromeros

Ceromeros. El termino proviene de CERAMIC-OCTIMIZED- POLIMER. O polimeros optimizados con particulas o carga ceramica. son materiales nuevos que se emplean para la elaboración de incrustaciones, coronas y puentes.

shing
Download Presentation

Ceromeros

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Ceromeros

  2. El termino proviene de CERAMIC-OCTIMIZED- POLIMER. O polimeros optimizados con particulas o carga ceramica

  3. son materiales nuevos que se emplean para la elaboración de incrustaciones, coronas y puentes. Se trata de un polímero optimizado que incorpora en su composición finísimas partículas de cerámica y fibras reforzadas.

  4. Material híbrido de una resina y porcelana (relleno inorgánico) el cual da un buen resultado estético y un gran comportamiento clínico.

  5. Propiedades fisico mecanicas muy superiores poseen : Exelentes caracteristicas en terminos de color Mimetizacion Translucidez Opacidad biocompatibilidad

  6. Propiedad de particular interes: Caracteristicas de resilencia. Muy util en concecuencia en restauraciones de protesis sobre implantes ademas de la cualidad de no producir desdgaste de la estructura dental antagoniosta.

  7. Sistemas basicos ART-GLASS BELLE-GLASS TARGIS-VECTRIS

  8. ART-GLASS Fabricado en alemania en 1995 Heraeus-kulzer Poseee una estructura de polimerizacion tri-dimensional con uniones cruzadas lo cual le imparte especiales propiedades fisico-mecanicas ademas de una alta resistencia al desgaste.

  9. Fracciones inorganiocas: Vidrio : vidrio de bario radio-opaco Tamaño de particula : 0.7 micrometros Silice coloidal Otros componentes: Accido silicico: para alta densidad, facilidad de modelado Microglass: vidrio de bario –aluminio de forma esferica Tamaño particlua: 0.07 micrometros

  10. AGENTES RETICULANTES : formacion de cadenas cruzadas “ esta fase inorganica esta silanizada para union con la fase organica

  11. FASE ORGANICA El denominado VITROID por la compañía HERAEUS-KULZER . Vidrio orgánico multifuncional logra enlaces tridimensionales de lata densidad. PROPIEDADES FISICO-MECANICAS Dureza = estructura dental Modulo elástico este factor es de trascendental importancia en la restauración sobre implantes.

  12. COMPÒRTAMIENTO ABRASIVO Es un simulador de masticación con proyección a 5 años el material muestra un desgaste minimo no desgasta los dientes antagonistas.

  13. INDICACIONES CLINICAS Material estetico sobre estructuras metalicas preparadas para la union con el sistema SILOC. elavoracion de carillas esteticas veneers Elavoracion de incrustaciones INLAY u ONLAY

  14. BELLE –GLASS Se introduce en el comercio dental en el año de 1996 inicialmente por la compañía BELLE y en la actualidad por KERR Compuesta de polimeros dimetacrilatos uretano y dimetacrilato alifaticos (OLIGOMERS ) Carga de vidrio de 74 % : boro- silicato Tamaño de particula 0.6 – 10 micrometros 87% de vidrio de bario y bisGMA

  15. Polimeriza en una camara a alta temperatura y presion en presencia de nitrogeno Permite polimerizacion en ausencia de oxigeno Asi alcanza un elevado grado de polimerizacion T de 140º centigrados Presion de nitrogeno : 80 l/pulgada en un tiempo de 10 a 20 minutos

  16. Dureza :90.7 (ciclo de 20 minutos) % de conversion : 98.5 buen comportamiento en zonas de choque masticatorio directo. Alto grado de polimerizacion Ausencia de poros gracias a la alta presion que es sometida durante el proceso de curado.

  17. La nueva BELLE GLASS(LOW THERMAL FORMULA) se ajusta a un coeficiente de expansión muy cercano al de la estructura dental (11.4) siendo así de 13.1 Propiedades físico –mecánicas Resistencia compresiva 442 Mpa Resistencia flexural 158 Mpa Resistencia tensil-diametral 63MPa Coeficiente de expansión térmica 13.1ppm/c Grado de conversión ç98.5%

  18. Cinta de refuerzo CONSTRUCT CINTA DE REFUERZO DE POLIETILENO , DE ALTO PESO MOLECULAR , TRATADA CON PLASMA , PRESILANIZADA E INPREGNADA CON RESINA: *ferulizacion periodontal *ferulizacion post-ortodoncia *cinta de refuerzo en las coronas de ceromero libre de metal *protesis adhesiva , como refuerzo entre los dientes puilatres y el pontico a reemplazar.

  19. SISTEMA TARGIS-VECTRIS IVOCLAR Incluye en su matriz organica polimeros de refuerzo o carga de finas particulas ceramicas en forma tridimensional. Polimeriza en camaras especiales con luz y calor. Es de resina compuesta reforzado con fibras de vidrio silanizadas.

  20. Composicion de TARGIS COMPOSICION ESTANDAR TARGIS DENTINA TARGIS INCISAL Bis-GMA 9.0 8.7 Decandiol dimetacrilato 4.8 4.6 Dimetacrilato de uretano 9.3 9.0 Vidrio de bario silinizado 46.2 72.0 Oxido mixto silinizado 18.2 Si o2 altmentealtamente disperso 11.8 5.0 Catalizadortes estabilizadores 0.6 0.6 Pigmentos - 0.1 -0.1 % en peso

  21. Propiedades fisico-mecanicas p. Fisicas T DENTINA T. INCISAL Resistencia flexion 170+-20MPa 200+-20MPa Modulo elastico 12300+-900MPa 11000+-1200MPa Dureza vickers 640+-60MPa 700+-60MPa Sorcion de agua 16.5+- 1.2 ug/mm3 16.5+- 1.2 ug/mm3 Contenido de carga 55.9% en volumen 55.5% en volumen 76.2 en peso 77.0% en peso

  22. Composicion del VECTRIS COMPOSICION ESTANDAR SINGLE FRAME PONTIC Bis-GMA 38.6 35.2 24.5 Dencaldiol di metacrilato 0.5 0.4 0.3 Trietilenoglicoldimetacrilato 9.7 8.8 6.2 Di metacrilato de uretano 0.1 0.1 0.1 Si o2 altamente disperso 5.5 5.0 3.5 Catalizadores y estabilizadores <0.5 <0.4 <0.3 Pigmentos <0.1 <0.1 <0.1 Fibra de vidrio 45.0 50.0 65.0 % en peso

  23. Propiedades p. Fisicas single frame ponti Resistencia flexion 700+-70mpa 700+-70mpa 1300+-60mpa Modulo elastico 21000+-1800mpa 21000+-1800mpa 36000+-2500mpa Sorcion de agua 18.8+-0.8ug/mm3 18.8+-0.8ug/mm3 Solubilidad en agua 0.8+-0.25ug/mm3 0.8+-0.25ug/mm3

  24. Indicaciones clinicas Coronas completas en anteriores o posteriores sin metal Carillas laminadas :veneers Incrustaciones inlay y onlay Protesis fijas de 3 unidades sin sustrato metalico Material estetico (blindaje) para recubrimiento de estructuras metalicas en protesis fijas de tramo largo

  25. INDICACIONES GENERALES PARA LAS PREPARACIONES QUE VAN A SER RESTAURADAS CON CEROMEROS

  26. PREPARACION PARA CORONA COMPLETA LIBRE DE METAL EN POSTERIORES -reduccion homogenea en cra oclusal de 1.5 a 2 mm. Siguinedo contorno morfologico del diente -desgaste vestibular, lingual y proximal de 1.5 mm -linea terminal en hombro redondeado o chanfer profundo , muy definido en todo el contorno de 360º -todo el contorno debe ser redondeado , suave , sin presencia de angulos agudos.

  27. PREPARACION PARA DIENTES ANTERIORES -reduccion homogenea con desgaste incisal de 1mm , linea terminal definida en chanfer profundo de 0.6 a 0.8 mm -todos los contornos redondeados

  28. PREPARACION PARA RESTAURACIONES INLAY -reduccion en la zona central , oclusal , con una profundidad de 1.5 mm apartir de la cuspide antagonista -paredes laterales con una divergencia de 6 8º -todos los angulos diedros o triedros redondeados . utilize siempre fresas de diamante redonda -pared gingival en lo posible supra -paredes vestibulares y lingual de la caja proximal ligeramente abiertas -angulo cavo supeficial , suavemente redondeado sin biseles

  29. PREPARACIONE ONLAY -los mismos lineamientos de la preparacion INLAY -la cobertura cuspidea debe tener un desgaste de 1.5 a 2mm

  30. CEMENTOS PARA LA CEMENTACION DE RESTAURACIONES EN CEROMEROS

  31. Los cementos recomendados deben ser con base en formulas de resinas adhesivas , preferiblemente dentro de la misma formulacion del ceromero.

  32. RESTAURACIONES EN TARGIS-VECTRIS: -preparacion de la cara interna de la restauracion mediante microaireado , con un chorro de oxido de aluminio de 50 micrometros. -lavado profuso y secado con aire limpio -aplicación de una capa delgada y continua de silano-monobond s-aireado -Pincelar una delgada capa de helioobond Profilaxis con cepillo suave y bicarbonato de sodio. -aplicación de acido fosforico por 10 segundos -aplicacion de adhseivo EXCITE

  33. aireamos suavemente • -mezcla de la jeringa base y catalizadora de la resina cementante –variolinK II • -aplicarla en capa delgada en la cara noble de la restauración • -llevarla a posición sobre la preparación cavitaria con suave presion • Retirar los excesos • Colocar bandas proximales y manteniendo la presión sobre la restauración • Fotopolimerizar por 40 sg cada una de las caras • oclusal, Proximal mesial por vestibular • Proximal distal por vestibular • Proximales por lngual

  34. -Control de oclusión y de contactos con seda dental -pulimiento suave de todos los bordes con una copa o rueda siliconada –ASTROPOL

  35. CEMENTACION DE LA CORONA COMPLETA • -Después del paso de profilaxis en la estructura dentaria, NO GRABAMOS CON ACIDO FOSFORICO • -Aireamos suavemente sin desecar la dentina • Aplicación del sistema adhesivo • -los bordes periféricos de la restauración – interfaz ceromero- cemento-estructura dentaria se cubren con un gel traslucido previo0 a la polimerización • -Este gel impide la acción inhibidora del oxigeno en la polimerización de la resina cementante