An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. DEMİR – KARBONALAŞIMLARI

  2. Sıvı 1537 d - ferrit 2.96 Å (HMK) A4 1394 g - ostenit 3.56 Å (YMK) A3 911 a - ferrit 2.86 Å 769 Curie noktası, A2 (HMK) Zaman Allotropik (polimorf) Dönüşüm : Bir malzemenin farklı sıcaklılarda farklı kristal yapıya dönüşmesine denir.

  3. Fe-C denge diyagramında izotermal reaksiyonları gösteren üç yatay çizgi vardır: • Peritektik reaksiyon • Ötektik reaksiyon • Ötektoid reaksiyon 1493 oC sıcaklıkta bulunan yatay çizgi peritektik reaksiyonu göstermektedir. Peritektik reaksiyon şöyle yazılabilir: Sıvı (L) +δ↔ γ

  4. İkinci yatay çizgi, 1147 oC sıcaklıkta bulunan çizgidir. Bu çizgi, aşağıdaki verilen reaksiyonun meydana geldiği ötektik sıcaklığı çizgisidir. Sıvı (L)  + Fe3C En son yatay çizgi 723 oC sıcaklıkta oluşur. Bu çizgiye ötektoid sıcaklığı çizgisi denir.Ötektoid reaksiyon şöyle yazılabilir. γ (östenit)α+ Fe3C