Possibilities Of Aluminium Extrusion By The ECAP Method

Possibilities Of Aluminium Extrusion By The ECAP Method. Miroslav Greger - VŠB – Technical University o f Ostrava Stanislav Rusz - VŠB – Technical University o f Ostrava. Introduction.

becky
Download Presentation

Possibilities Of Aluminium Extrusion By The ECAP Method

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Possibilities Of Aluminium Extrusion By The ECAP Method Miroslav Greger - VŠB – Technical University of Ostrava Stanislav Rusz - VŠB – Technical University of Ostrava

  2. Introduction The technology ECAP allows to obtain an ultra-fine grain in larger volumes,moreover without change of original cross-section of the input semi-product. It is possible to use the obtained materials in automotive industry, in military and aerospace industries.

  3. Principles of ECAP Fig. 1. Schematic illustration of equal channel angular pressing process (ECAP)

  4. Principles of Shearing on Passage Through the ECAP Die Route A Route BA 90° Route BC Route C 90° 180° Fig. 2. The four processing routes in ECAP

  5. Shearing Patterns Associated with the Different Processing Routes Z plane X plane Y plane X Z Z Y Y X Fig. 3. Shearing associated by a single passage through the die

  6. Influences of the Forming Parameters on Plastic Deformation • Influence of inner energy • Non-homogeneity of deformation • Density of dislocation • Concentration of vacancies

  7. Change of Dislocation Substructure Fig. 4. Scheme of change of dislocation sub-structure after cold deformation

  8. Dependencies Linear dependence of dislocation density: Flow stress necessary for continuing of deformation:

  9. Experimental Verification Fig. 5. Overall view on the forming equipment and die Fig. 6. Detailed view on the extruding punch for the ECAP technology

  10. 50 m Samples for Extrusion Fig. 7. Initial sample and samples after extrusion Fig. 8. Structure in the central area

  11. Deformation Resistance Fig. 9. Deformation resistance of the aluminium Fig. 10. Deformation resistance of the alloy AlCuMg

  12. 50 m 50 m Micro-structure of Sample After Extrusion Fig. 11. The first passage Fig. 12. The second passage Fig. 13. The third passage Fig. 14. The fourth passage

  13. Conclusion • Refining of grain in poly-crystalline metals. • Micro-structure obtained by ECAP method depends on: • Using of more passes and turning of the sample. • Extruding the sample by 4 or more passes. • Optimal angle between horizontal and vertical channel of the part is ≈ 90 degrees. Radius of fillet of the extrusion channel must correspond to conditions for steady flow of metal. • Strain rate has only partial influence on deformation resistance and small influence on micro-structure.

  14. Practical Illustration of the ECAP Method by Mathematic Modeling Fig. 15. The example of stress intensity by the simulation process of the AlCuMg extrusion (1st and 2nd sample)

  15. Practical Illustration of the ECAP Method by Mathematic Modeling Fig. 16. The example of shear stresses partition bythe ECAP method (1st a 2nd sample)

  16. Practical Illustration of the ECAP Method by Mathematic Modeling Fig. 17. Contact pressure between sample and tools for AlCuMg alloy by the ECAP method(1st a 2nd sample)

  17. Practical Illustration of the ECAP Method by Mathematic Modeling Fig. 18. The example of the deformation intensity of AlCuMg alloy by the ECAP method (1st a 2nd sample)

  18. Practical Illustration of the ECAP Method by Mathematic Modeling Fig. 19. The example of the lay-out of temperature of AlCuMg alloy by the ECAP method (1st a 2nd sample)

  19. Thank you for your attention