1 / 28

Tiras de carga e supercondutividade

Tiras de carga e supercondutividade. Thiago Tunes. HgBa 2 Ca 2 Cu 3 O 9 (sob pressão). 160. 140. HgBa 2 Ca 2 Cu 3 O 9. TlBaCaCuO. 120. BiCaSrCuO. 100. YBa 2 Cu 3 O 7. N Líquido (77K). 80. 60. ( LaBa)CuO. 40. Nb 3 Ge. Nb 3 Sn. NbN. NbC. 20. Nb. Pb. Hg. V 3 Si. 1910.

alaqua
Download Presentation

Tiras de carga e supercondutividade

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Tiras de carga e supercondutividade Thiago Tunes

  2. HgBa2Ca2Cu3O9 (sob pressão) 160 140 HgBa2Ca2Cu3O9 TlBaCaCuO 120 BiCaSrCuO 100 YBa2Cu3O7 N Líquido (77K) 80 60 (LaBa)CuO 40 Nb3Ge Nb3Sn NbN NbC 20 Nb Pb Hg V3Si 1910 1930 1950 1970 1990 Materiais Supercondutores Temperatura de transição supercondutora (K) BCS (30K)

  3. Os supercondutores de alta temperatura crítica Bednorz e Müller 1986 Nobel em 1987

  4. Os supercondutores de alta temperatura crítica O primeiro (1986): LaBaCuO 40 K / -233 ºC YBaCuO 92 K / -181 ºC O mais estudado: O recorde: HgTlBaCaCuO 138 K / -135 ºC Aguardando confirmação… InSnBaTmCuO 150 K / -123 ºC

  5. Diferenças fundamentais Alta TC Planos de CuO  cupratos Proximidade de uma fase magnética Estado normal metálico ou isolante dependendo da dopagem Pseudogap Não são descritos pela teoria BCS

  6. A supercondutividade ocorre nos planos de cobre e oxigênio YBa2Cu3O7- Reservatório de elétrons ou buracos

  7. Diagrama de fases AF SUC STRIPES

  8. 0 Tc T Pseudo-gap    e R = 0 convencional R = 0    HTCS 0 T Tc T*

  9. Sem dopagem Isolante de Mott ANTIFERROMAGNÉTICO

  10. Com dopagem Buracos dopados nos HTCs NÃO se espalham uniformemente nos planos de CuO2 Tiras de carga Stripes Checkerboard Tabuleiro de xadrez Mais exótico…

  11. Nature 2004 x = 0.10 T = 100 mK High resolution STM topograph of CaCl plane Conductance map g(r,E) at E=24 meV 4a0 , 4a0/3 a0

  12. STRIPES La15/8 Ba 1/8CuO4 A "reciprocal space map" representation of the stripes in the copper-oxide layers of LBCO. "H" and "L" are measures of how often the ribbon-like stripes "wave." H corresponds to the a direction, and L corresponds to the c direction. Their reciprocals, 1/H and 1/L, are a measure of the stripes' wavelength. The red and pink vertical streak at H = 0.25 indicates that the stripes have a wavelength of four lattice parameters and are stacked along the c direction. Nature Physics 2005

  13. Stripes fase listrada La(2-x-y)NdySrxCuO4 + = e Onda de densidade de carga  CDW

  14. Ondas de densidade de carga e ondas de densidade de spin Separemos os elétrons em duas “espécies”: spin- e spin-

  15. Metal Normal CDW SDW posição

  16. Fase listrada melhor observada num “primo” dos supercondutores Formação de CDW [onda de densidade de carga] novo ingrediente: ordenamento direcional dos orbitais d do Mn

  17. Acredita-se que nos HTCS haja um equilíbrio entre o ordenamento de spin (AFM, nao SDW) e o ordenamento de cargas (tipo CDW) ao longo de uma direção ( na Fig.): As cargas tendem a se agrupar em regiões de menor ordem AFM

  18. Modelo tJ Campo médio r=ty/tx

  19. O aumento de Tc é um efeito de campo médio ? Campo médio X QMC

  20. Thiago O modelo de Hubbard com hopping anisotrópico QMC

  21. Modelo de Hubbard com hopping anisotrópico H= tx=t r=ty/t

  22. Anisotropia tx=t ty r=ty/t<<1 Direção preferencial de movimento das cargas

  23. Por onde começar =1 Mais simples { r=0.1 r=0.01 r=0.001 U=4

  24. ~ 6 realizações de 500 warms 4000 sweeps L=6, 8, 10 e 12 L=14 se precisar { Aumentar até Ps e AF estabilizarem  Depende do tamanho do sistema

  25. SUPERCONDUTIVIDADE Traçar Ps como função de  Extrair  se 0 Traçar Ps/L2- como função de  Estimar TC Densidade superfluida: depois

  26. SUPERCONDUTIVIDADE Outras simetrias para  S-wave, sx-wave, d-wave s-wave: (corr. fn, no vertex) 0.1393727 +- 0.0005059 0.0000000 +- 0.0000000 sx-wave: 0.3507235 +- 0.0007571 0.0000000 +- 0.0000000 d-wave: 0.3486298 +- 0.0007491 0.0000000 +- 0.0000000 Qual a mais favorável ?

  27. MAGNETISMO Traçar AF como função de  Extrair M Traçar F como função de  TC =0 Mermin-Wagner : depois F ou AF ?

  28. No futuro próximo condutividade METAL ou ISOLANTE? xy { ISOLANTE (T) METAL