Piezoelectric Displacement Results of Measuring Pt/PNZT/Pt Capacitor on Seiko Instruments SPA400 AFM.

Piezoelectric Displacement Results of Measuring Pt/PNZT/Pt Capacitor on Seiko Instruments SPA400 AFM. . Radiant Technologies, Inc. August 7, 2001. Sample Description. Capacitor Area: 12µ x 12µ Construction: Pt/PNZT/Pt Composition: 4/20/80 PNbZT PNZT Thickness: 1 µm. Displacement at 40V.

argyle
Download Presentation

Piezoelectric Displacement Results of Measuring Pt/PNZT/Pt Capacitor on Seiko Instruments SPA400 AFM.

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Piezoelectric Displacement Results of Measuring Pt/PNZT/Pt Capacitor on Seiko Instruments SPA400 AFM. Radiant Technologies, Inc. August 7, 2001

  2. Sample Description • Capacitor Area: 12µ x 12µ • Construction: Pt/PNZT/Pt • Composition: 4/20/80 PNbZT • PNZT Thickness: 1µm

  3. Displacement at 40V Displacement measured at 40Vwith a measurement period of 1 second.

  4. Displacement at 40V Displacement loop averaged 10 times.

  5. Nested Displacement Loops Displacement measured at 40V, 30V, 20V, and 10V. Measurement period is 1 second.

  6. Conclusion • Precision Premier integrates with the Seiko Instruments AFM family to collect displacement measurements of thin ferroelectric films. • The 1µm thick Radiant 4/20/80 PNbZT film displaced 23Å at 40V giving the film a d33 value of 57.5. • The measured value is the not the true d33value of the film due to strong clamping by the substrate. • Piezoelectric fatigue, frequency response, and imprint can also be measured using the Vision software.