An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Principle of the process Structure Process modeling Defects Design For Manufacturing (DFM) Process variation Metal forming Drawing Handout 8 c

  2. Bulk Drawing: Engineering Analysis 1. Introduction In the bulk deformation processes, drawing is an operation in which the cross section of a bar, rod, or wire is reduced by pulling it through a die opening, as shown in Figure 1. Handout 8 c

  3. Extrusion Drawing Has pushing force Has pulling force Figure 1 here Handout 8 c

  4. Bulk Drawing: Engineering Analysis 2. Objectives of the Analysis Rolling process Drawing process Torque (force) Power Velocity (productivity) Max draft Pulling force Power Pulling velocity Max draft Handout 8 c

  5. 3. Mechanics Phenomenon There is a tensile stress due to pulling force, but compression still plays a significant role since the metal is squeezed down as it passes through the die opening. Handout 8 c

  6. r=(A0-Af)/A0 4. Parameters r: area reduction A0: initial area of work Af: final area d=D0-Df, draft Drawing stress Contact length Die angle Friction between work and die Force Handout 8 c

  7. Accounts for inhomogeneous deformation 5. Drawing stress, drawing force, power Handout 8 c

  8. 5. Drawing stress, drawing force, power Handout 8 c

  9. - If done, as Reduction , draw stress also Allowable power Yield stress 6. Limit of Drawing Maximum power < Allowable power of a drive system If not, material goes into plastic region & no “drawing” occurs, just “elongation” Maximum stress < Yield stress Entire reduction not done in a single pass (done in steps) Handout 8 c

  10. 6. Finding Max draw stress & Max reduction (1 pass) Assumption: no friction, no strain hardening (n=0), no redundant work (perfectly plastic) Max. draw stress = Yield Strength Also, because (n=0) Handout 8 c

  11. Handout 8 c

  12. Example Wire stock of initial diameter = 0.125 in. is drawn through two dies each providing a 0.20 area reduction. The staring metal has a strength coefficient = 40,000 lb/in.2 and a strain hardening exponent =0.15. Each die has an entrance angle of 12o, and the coefficient of friction at the work-die interface is estimated to be 0.10. The motors driving the capstans at the die exists can each deliver 1.50 hp at 90% efficiency. Determine the maximum possible speed of the wire as it exits the second die. Handout 8 c

  13. Handout 8 c

  14. Handout 8 c

  15. From this calculation, the velocity of the second die is the limiting velocity. That is to say, the velocity of the whole system should take 3.47 ft /s. As a result, • the first operation would have to be operated at well below its maximum possible speed; or • the second draw die could be powered by a higher horsepower motor; or • the reductions to achieve the two stages would be reallocated to achieve a higher reduction in the first drawing operation. Handout 8 c