SCIART: ALD oxide films as diffusion barriers for silver artifacts

SCIART: ALD oxide films as diffusion barriers for silver artifacts. Raymond J. Phaneuf, University of Maryland College Park, DMR 1041809.

dafydd
Download Presentation

SCIART: ALD oxide films as diffusion barriers for silver artifacts

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. SCIART: ALD oxide films as diffusion barriers for silver artifacts Raymond J. Phaneuf, University of Maryland College Park, DMR 1041809 Al2O3 ALD coatings and brush applied (NC) and flow coated (NCFC) nitrocellulose coatings after aging at elevated H2S levels show thicker ALD oxide films affect the color of the object less before aging and last longer than the organic nitrocellulose lacquer. This translates to better protection of art objects with less work on the part of conservators. Bare silver 2x coated nitrocellulose Brushed nitrocellulose ΔE 100nm Al2O3 70nm Al2O320nm Al2O3 (ALD) Level of reversibility of ALD oxide film application, via NaOH chemical etching vs. mechanical polishing using precipitated chalk and alumina polishing powders was investigated. While inductively coupled plasma mass spectrometry (ICP-MS) indicates that NaOH preferentially etches copper out of sterling silver, we find that at low NaOH concentrations etching the oxide removes significantly less metal than polishing techniques currently used by conservators.

More Related