“Properties of Concrete” Introduction

“Properties of Concrete” Introduction. Overview. What is concrete made of? What Is Concrete Used For? Why Is Concrete Used? Why Do We Reinforce Concrete? Curing of concrete. What is concrete made of?. What is concrete made of?. Concrete is basically a mixture of two components: Paste

dahlia
Download Presentation

“Properties of Concrete” Introduction

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. “Properties of Concrete”Introduction

  2. Overview • What is concrete made of? • What Is Concrete Used For? • Why Is Concrete Used? • Why Do We Reinforce Concrete? • Curing of concrete

  3. What is concrete made of?

  4. What is concrete made of? • Concrete is basically a mixture of two components: • Paste • Aggregates • Paste (Portland cement, water, and air) • Aggregates (sand, gravel, crushed stone)

  5. CEMENT • Cement (Dry powder of very fine particles) is a building material made by grinding calcined limestone and clay into a fine powder • Portland Cement chemical composition • Limestone, shale and clay • CaO (lime) • Al2O3 (Alumina) • SO3 (Sulfite)

  6. CEMENT • When mixed with water, forms a paste • it undergoes chemical changes (chemical reaction-Hydration) • Glue paste coats all the aggregates together • hardens and forms a solid mass

  7. WATER • Water good for drinking is good for concrete……

  8. WATER • needed for two purposes: • chemical reaction with cement • workability • only 1/3 of the water is needed for chemical reaction • extra water remains in pores and holes • results in porosity • Good for preventing plastic shrinkage cracking and workability • Bad for permeability, strength, durability.

  9. AGGREGATES • cheap fillers • hard material • provide for volume stability • reduce volume changes • provide abrasion resistance

  10. AGGREGATE • Aggregate are divided into two groups: • Fine - AASHTO M-6 or ASTM C-33 • Coarse - AASHTO M-80 or ASTM C-33 • Fine aggregate consist of natural or manufactured sand with particle size up to 3/8 inch • Coarse aggregate particles are retained on the #4 sieve and range up to 6 inches

  11. COARSE AGGREGATE

  12. FINE AGGREGATE

  13. CONSTITUENTS • paste 25 to 40% • portland cement 7% to 15% by Vol. • water 14% to 21% by Vol. • Aggregates 60% to 75% • coarse aggregates • Fine aggregates • Admixtures

  14. CONSTITUENTS Cement Water Air Fine Aggregate Coarse Aggregate Cement paste constitutes about 25% to 40% volume of concrete

  15. AIR ENTRAINED CONCRETE • Why the difference between line #1 and line #2? • Line 1, small size CA, increased H2O and cement • Line 2, larger CA, less H20, air, cement

  16. NON-AIR ENTRAINED CONCRETE CementWater Air Fine Aggregate Coarse Aggregate • Similar to Air Entrained Concrete slide • See how aggregate size impacts water demand and amount of “paste” in the mix

  17. increase set time decrease set time increase workability adjust other concrete properties reduce water demand entrain air inhibit corrosion ADMIXTURES • Plastic and hardened properties of concrete may be changed by adding admixtures • Admixtures are commonly used to:

  18. ADMIXTURES • chemical • retarders • accelerators • water reducing • air entraining • mineral • fly ash • silica fume • slags

  19. QUALITY OF CONCRETE • Quality of concrete depends on quality of paste and quality of aggregates • each particle of aggregate is completely coated with paste • All spaces between aggregate is filled with paste

  20. QUALITY OF CONCRETE Is determined by: • W/C Ratio – • Advantage of reducing water • Increased compressive and flexural strength • lower permeability • increased resistance to weathering • reduced shrinkage cracking tendencies • The less water used, the better quality of concrete, provided it can be consolidated properly.

  21. Ten cement-paste cylinders with water-cement ratios from 0.25 to 0.70. The band indicates that each cylinder contains the same amount of cement. Increased water dilutes the effect of the cement paste, increasing volume, reducing density, and lowering strength.

  22. FORMS • A form is the mold for setting concrete into a desired shape

  23. What Is Concrete Used For?

  24. What Is Concrete Used For? • Construction Material Art Work

  25. Picture of Bench

  26. Why Is Concrete Used?

  27. Why Is Concrete Used? • Economics • Inexpensive, readily available • Material Properties • Long Lasting • Molded into a desired shape • Great insulator • Hard

  28. Material Properties (cont.) • Great Compressive Strength (up to 8000 psi and even more than that) • Poor Tensile Strength (almost 0) • Reinforcement methods ($)

  29. Why Do We Reinforce Concrete?

  30. Why Do We Reinforce Concrete? • Prevent cracking due to tension forces

  31. Question • What is the difference between tension and compression?

  32. Question • Why would concrete never be used in tension?

  33. How Do We Reinforce Concrete? • Steel rebar • Excellent in tension, poor in compression

  34. CURING OF CONCRETE

  35. CURING OF CONCRETE • Over time concrete will cure, which is a hardening process. • Concrete has a 28 day curing time, this is the amount of time it takes to be considered completely cured

  36. Curing • Critical to durable concrete • Increases strength • Decreases permeability • Increases durability

  37. Curing Concrete • How concrete is cured: • Ponding or Immersion • Spraying or Fogging • Wet Coverings • Impervious Paper • Plastic Sheets • Membrane-Forming Curing Compounds

  38. Questions? • Remember: • Use Common Sense • Temperature effects on your body have very similar effects on concrete • If you are not sure, ASK!!!