Polymer Analyses GPC, TEM, SEM

Polymer Analyses GPC, TEM, SEM. Speaker : 王睿詡 Date : 2009/11/23. Outline. GPC (Gel Permeation Chromatography) TEM (Transmission Electron Microscopy) SEM (Scattering Electron Microscopy). GPC (Gel Permeation Chromatography, Size Exclusion Chromatography). A Kind of LC Mechanisms.

denzer
Download Presentation

Polymer Analyses GPC, TEM, SEM

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Polymer AnalysesGPC,TEM, SEM Speaker : 王睿詡 Date : 2009/11/23

  2. Outline • GPC(Gel Permeation Chromatography) • TEM (Transmission Electron Microscopy) • SEM (Scattering Electron Microscopy)

  3. GPC (Gel Permeation Chromatography, Size Exclusion Chromatography)

  4. A Kind of LC Mechanisms • Gel-Permeation Chromatography is a • mechanical sorting of molecules based • on the size of the molecules in solution. • Small molecules are able to permeate • more pores and are, therefore, retained • longer than large molecules. LC Separation Mechanisms Ref. : Rubinson and Rubinson, Contemporary Instrumental Analysis, Prentice Hall Publishing.

  5. Filter (ca 0.5 um) GPC Columns Pump Injector Loop To Waste Concentration Detector Optional Detector #1 e.g. Viscosity Optional Detector #2 e.g Light Scattering To Waste To Waste To Waste Flow Voids: Uniform Diameter D helps minimize voids Pore: Size is given by the correlation length x x D = 1 - 50 mm Structural Picture

  6. Column of GPC Hydrodynamic radius (Stoke’s radius) • K = cS /cM = (Ve - Vo)/Vi, since Vt = Vi + Vo + VG • (Vi is the volume of solvent held in its pores) • (Vg is the volume occupied by the solid matrix of the gel) • (Vo is the free volume outside the gel particles.) • K is distribution coefficient, we assume that • VG ≈ 0 • Both are normally values between 0 and 1 • Molecules that are too big to penetrate any of the pores elute in Vo and give K = 0 • Molecules that are small enough to penetrate all of the pores elute in Vi + Vo and give K = 1 • Between 0 and 1, larger molecules give smaller K values. • If a molecule gives a K larger than 1, it is likely interacting with the gel beads themselves (adsorption).

  7. Retention Time vs. Molecular Weight

  8. Calibration Curve of GPC

  9. Common Detectors • UV – one of most common • Fluorescence – much greater sensitivity than UV • Refractive Index – widely used general detector • Electrochemical – based on amperometry, polarography, coulometry, • or conductometry. High sensitivity, wide applicability range • Mass Spectrometry – becoming increasingly used since interfacing • problems figured out. Expensive.

  10. GPC Analysis Cheng-Jyun Huang and Feng-Chih Chang* Macromolecules 2008, 41, 7041-7052

  11. GPC Analysis Chih-Feng Huanga, Hsin-Fang Leea, Shiao-Wei Kuoa, Hongyao Xua,b, Feng-Chih Changa,* Polymer 45 (2004) 2261–2269

  12. GPC Analysis Chih-Feng Huang, Shiao-Wei Kuo, Hsin-Fang Lee, Feng-Chih Chang* Polymer 46 (2005) 1561–1565

  13. TEM (Transmission Electron Microscopy) SEM (Scanning Electron Microscopy)

  14. Size !! 肉眼可見物體的範圍:~10-3m 光學顯微鏡(OM)可見的範 圍:~10-6m 掃描式電子顯微鏡(SEM)可 見的範圍: ~10-8m (~10 nm) 穿透式電子顯微鏡(TEM)可 見的範圍: ~10-10m (~0.1 nm)

  15. TEM (Transmission Electron Microscopy) From 交通大學貴儀中心

  16. TEM (Transmission Electron Microscopy) • When E0-ΔEvalues become smaller, the Images become darker; When E0-ΔEvalues • become bigger, the Images become lighter. http://www.jeol.com/tem/jem2100f.html

  17. Scanning Electron Microscope (SEM) From 交通大學貴儀中心

  18. Structural Image of SEM http://cem.ess.nthu.edu.tw/K12/Article.asp?ColId=7806A63102F19

  19. Principle of Imaging 0~50 ev

  20. EDX(S) and WDX(S) http://en.wikipedia.org/wiki/Wavelength_dispersive_X-ray_spectroscopy

  21. Images are Different Between in TEM and SEM SEM Image OM Image TEM Image

  22. Material Science Angew. Chem. Int. Ed. 2002, 41, 688

  23. Self-organization Morphology Solution state Bulkstate N : polymerization index χ: Flory-Huggins interaction parameter ƒ A : volume fraction of block A in the block copolymer Angew. Chem. Int. Ed. 2002, 41, 688

  24. TEM (Transmission Electron Microscopy) Ref : Wan-Chun Chen,† Shiao-Wei Kuo,*,‡ U-Ser Jeng,§ and Feng-Chih Chang*,† Macromolecules 2008, 41, 1401-1410

  25. TEM (Transmission Electron Microscopy) Ref : Shiao-Wei Kuo a,*, Pao-Hsaing Tung b, Feng-Chih Chang b European Polymer Journal 45 (2009)

  26. TEM (Transmission Electron Microscopy) Ref : Chu-Hua Lu,† Chih-Feng Huang,† Shiao-Wei Kuo,‡ and Feng-Chih Chang*,† Macromolecules 2009, 42, 1067-1078

  27. TEM (Transmission Electron Microscopy) Ref : Yuung-Ching Sheen a, Chu-Hua Lu a, Chih-Feng Huang a, Shiao-Wei Kuo b, Feng-Chih Chang a,* Polymer 49 (2008) 4017–4024

  28. Scanning Electron Microscope (SEM) Y.-C. Yen et al. Polymer 49 (2008) 3625–3628 SHIH-CHI CHAN,1 SHIAO-WEI KUO,1 HWO-SHUENN SHE,2 HO-MAY LIN,1 HSIN-FANG LEE,1 FENG-CHIH CHANG1 Journal of Polymer Science: Part A: Polymer Chemistry, Vol. 45, 125–135 (2007)

  29. Scanning Electron Microscope (SEM) Pao-Hsaing Tung, Shiao-Wei Kuo,*Shih-Chien Chan, Chih-Hao Hsu, Chih-Feng Wang, Feng-Chih Chang* Macromol. Chem. Phys. 2007, 208, 1823–1831

  30. Scanning Electron Microscope (SEM) Chih-Feng Wang,1 Shih-Feng Chiou,2 Fu-Hsiang Ko,3 Cheng-Tung Chou,2 Han-Ching Lin,1 Chih-Feng Huang,1 Feng-Chih Chang*1; Macromol. Rapid Commun. 2006, 27, 333–337

  31. Conclusion • Micro-Structural Analysis– TEM, SEM • Molecular Weight Determination - GPC

  32. Thank You for Your Attention