XRD and SEM analysis. Name: Guogen Liu Advisor: Prof. Chin Co-advisor: Prof. Barat Date: 07/24/2010. 1. Glass and TCO. 2. CdS. CdS is amorphous(XRD) and uneven in surface(SEM). Both CdS layers (CBD or Sputtering) are amorphous(XRD) CdCl2 treatment didn’t result

dexter-kennedy
Download Presentation

Name: Guogen Liu Advisor: Prof. Chin Co-advisor: Prof. Barat Date: 07/24/2010

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. XRD and SEM analysis Name: Guogen Liu Advisor: Prof. Chin Co-advisor: Prof. Barat Date: 07/24/2010

  2. 1. Glass and TCO

  3. 2. CdS CdS is amorphous(XRD) and uneven in surface(SEM)

  4. Both CdS layers (CBD or Sputtering) are amorphous(XRD) CdCl2 treatment didn’t result in crystallization There are lots of impurities on the surface which result in uneven

  5. From the XRD of one peak, we can make sure CdS layer is amorphous

  6. 1. CdTe CdTe before CdCl2 Grain size of the first peak g=81.5nm g=90nm CdTe after CdCl2

  7. The CdTe grain size is very small, less than 100nm. After CdCl2 treatment, it increases a little.

  8. CdCl2 treatment increase CdTe grain size and crystallization

  9. Thank you ?

  10. Conclusion: a, TCO surface should be clean completely b, Add a thin resistivity buffer layer between TCO and CdS c, CdS is not uniform and too much defect after CdCl2 treatment d, the grain size of CdTe is too small, close to amorphous d, Oxygen is necessary in the growth of CdTe crystal e, Vapor CdCl2 treatment is very important f, It is better to increase CdTe deposition temperture g, back contact and Cu doping can affect efficiency greatly h, Pay more attention on the interface between each layer i, try to convert thermal evaporation to CSS which is much mature j, try to do each step successfully first, then step by step