Physical properties of kafirin films Enviropak final meeting

Physical properties of kafirin films Enviropak final meeting. Mats Stading Katarina Nilsson Susanna Edrud Siw Kidman Annika Altskär Paola Olofsson Maria Petersson. SIK – The Swedish Institute for Food and Biotechnology Structure and Material Design Göteborg, Sweden. Samples.

fredericka-nolan
Download Presentation

Physical properties of kafirin films Enviropak final meeting

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Physical properties of kafirin films Enviropak final meeting Mats Stading Katarina Nilsson Susanna Edrud Siw Kidman Annika Altskär Paola Olofsson Maria Petersson SIK – The Swedish Institute for Food and Biotechnology Structure and Material Design Göteborg, Sweden

  2. Samples • Kafirin from CSIR large batch • Defatted zein from Sigma • Cast and thermoplastic films (from Sammy) • Plasticizer/protein: 0, 0.2, 0.3 and 0.4

  3. Characterization • Fracture strength (E, sb, eb) • Thermomechanical properties, DMA (G*, Tg) • Barrier properties (WVP, OP) • Moisture content • Microstructure (LM, CLSM, TEM)

  4. Plasticizers tested

  5. Stress at break sb [MPa] Ethanol Acetic acid Plasticizer/kafirin

  6. Strain at break eb [MPa] Ethanol Acetic acid Plasticizer/kafirin

  7. Moisture content MC [% w/w] Ethanol Acetic acid Plasticizer/kafirin

  8. Glass transition temperature ofkafirin and zein films Glycerol/PEG/la 1:1:1 Zein PEG LA PEG Kafirin Thermoplastic zein films from IMBC

  9. Water Vapour PermeabilityComparison with other materials WVP [g mm/m²h kPa] Whey protein glycerol Amylose Amylopectin glycerol sorbitol EVOH LDPE 0.4 0.48 0.83 Plasticizer/kafirin

  10. LDPE 1900 UP kafirin preparation Whey protein glycerol Amylose Amylopectin glycerol EVOH sorbitol 0.4 0.3 0.83 Oxygen Permeability OP [cm³ mm/m² d kPa] Plasticizer/kafirin

  11. Ethylene Permeability

  12. Thermoplastic zein films 25% PEG400, 50rpm, 60°C, 600s Micropores 0.1mm Fine structures of zein films 1mm Processing temperatures (60°C, 70°C,80°C) do not seem to change themicrostructure of the thermoplastic films 1mm

  13. Thermoplastic kafirin films 60°C 80°C Observations Bigger micropores at higher processing temperature Less striated structure at higher processing temperature  more even melting No microstructural difference between lauric acid and PEG plasticization 20mm 20mm 1mm 1mm