Background:. Obtaining large bio-compounds: separation and purification process is very important. Problems of commercial adsorbents: disordered pore structure Consequence: No optimal absorbing. Effective size: 2.09 nm. 2.09 nm. http://www.ilexikon.com/images/2/2b/Vitamin_B12.png.

jameson-gardner
Download Presentation

ilexikon/images/2/2b/Vitamin_B12.png

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Background: Obtaining large bio-compounds: separation and purification process is very important Problems of commercial adsorbents: disordered pore structure Consequence: No optimal absorbing Effective size: 2.09 nm 2.09 nm http://www.ilexikon.com/images/2/2b/Vitamin_B12.png

  2. Background: Mesoporous carbon adsorbents: CMK-n (n: 1 to 9) Advantages on adsorbing: 1. High specific surface area: around 1300 m2/g. Large pore volume: around 0.8 cm3/g 2. Ordered nano porous structure (around 3 nanometres). Synthesis of mesoporous carbon: Hard template method: employing mesoporous silicate as a template. Mesoporous silicate: synthesized by sol-gel method employing tri-block co-polymer as a template. Zhao DY, Feng JL, Huo QS, Melosh N, Fredrickson GH,Chmelka BF, et al. Science 1998;279(5350):548–52. Ryoo R, Joo SH, Jun S. J Phys Chem B 1999;103(37):7743–6.

  3. Points worth mention: Factors matters to capacity of adsorbents • Physical: right pore size and big pore volume and specific surface area. • Chemical: proper surface chemical properties for guest molecules Their idea: • Coating of polymer PMMA (polymethyl methacrylate) on the surface of mesoporous channels to increase the compatibility between adsorbent and guest molecule. http://www.jergym.hiedu.cz/~canovm/polymery/polymera/pmma.gif

  4. Points worth mention:

  5. Points worth mention: Structural characteristics of the different carbons tested

  6. Points worth mention: They controlled the coating of PMMA on mesoporous carbon to be same.

  7. Points worth mention: • Adsorption of VB12 on the different adsorbents as a function of contact time.

  8. Points worth mention: • Justification of hydrogen bond between B12 and PMMA: IR spectra of (b) PMMA, (c) CMK-3-PMMA, (e) CMK-3-PMMA-VB12 in the C=O stretching region between 2100 and 1400 cm1.

  9. Conclusions: The VB12 adsorption capacities of the adsorbents depended on the BET surface area as well as mesoporous volume and pore diameter of the adsorbents. After coating with PMMA, they all exhibited higher adsorption than their initial mesoporous carbons. That was due to the formation of hydrogen bonding between PMMA on the mesoporous carbons surface and VB12 molecules. The adsorption properties were mostly influenced by the surface properties and the pore structure.