1 / 21

3D Modeling and Simulation of Hg 2 Cl 2 Crystal Growth by Physical Vapor Transport

3D Modeling and Simulation of Hg 2 Cl 2 Crystal Growth by Physical Vapor Transport. Joseph Dobmeier Advisor: Patrick Tebbe Minnesota State University November 2011. Introduction. Hg 2 Cl 2 crystals are useful for their acousto-optic properties.

jennis
Download Presentation

3D Modeling and Simulation of Hg 2 Cl 2 Crystal Growth by Physical Vapor Transport

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. 3D Modeling and Simulation of Hg2Cl2 Crystal Growth by Physical Vapor Transport Joseph Dobmeier Advisor: Patrick Tebbe Minnesota State University November 2011

  2. Introduction • Hg2Cl2 crystals are useful for their acousto-optic properties • Used to construct acousto-optic modulators and tunable filters in the low UV and long wave infrared regions 8-10μm[1] Image from Kima et. al., 2008 • Applications include: laser Q-switches, fiber-optic signal modulators, spectrometer frequency control

  3. Introduction • Two technologically mature and commercially available materials for this region are Terillium Oxide (TeO2) and Thalium Arsenide-Selenide (TAS) Image from http://www.olympusfluoview.com/theory/aotfintro.html • TeO2 is fragile and prone to damage • TAS is extremely toxic and requires specialized handling

  4. Introduction Images from Kima et. al., 2008

  5. Outline • Modeling • Simulation • Results • Future Research Directions

  6. Modeling • Four conservation equations[2-4]:

  7. Modeling • Geometry: • Vertically oriented 5x5cm cylinder with the source at the bottom • Boundary conditions: • Walls: no slip, adiabatic, and impermeable • Source and sink: constant temperature, tangential velocity of zero, normal velocity calculated using Fick’s law and Dalton’s law of partial pressures[6]

  8. Outline • Modeling • Simulation • Results • Future Research Directions

  9. Simulation • Performed by a commercially available code FIDAP, a product of Fluent Inc. • Capabilities extended to physical vapor transport process through the use of a subroutine • Subroutine determines the boundary nodal velocities by a finite difference calculation of the mass fraction derivatives • Each nodal velocity was then scaled to ensure source and crystal mass flux average values satisfied the continuity equation[2] • Initial conditions for velocity were zero, a linear profile was selected for the concentration profile

  10. Simulation • Mesh density: • Parametric studies were performed in 2D on the mesh density • Three sizes were compared: • 31x31 • 61x61 • 121x121 • Flowfield development was found to be identical, but some small-scale recirculation cells were not captured • A frequency analysis was undertaken comparing the oscillatory regions which agreed across densities

  11. Simulation

  12. Simulation • Table of parameters used in study (Ts = 330°C):

  13. Outline • Modeling • Simulation • Results • Future Research Directions

  14. Results • Case 1:

  15. Results • Case 2:

  16. Results • Case 5:

  17. Results Case 5 (0.33, 0, 0.5) Case 1 (0, 0, 0.5) Case 2 (0, 0, 0.5) Case 3 (0.49, 0, 0.4)

  18. Outline • Modeling • Simulation • Results • Future Research Directions

  19. Future Research • Complete bifurcation graph showing flowfield regime transition • Perform phase-space analysis of transient and oscillatory regions • Simulate more cases for current geometry • Modify geometry for different furnace layouts • Reduce total run time through parallel implementation of simulation with newer commercial software code

  20. Questions ???

  21. References [1] Joo-SooKima, Sudhir B. Trivedia, JolantaSoosa, NeelamGuptab, WitoldPalosza. Growth of Hg2Cl2 and Hg2Br2 single crystals by physical vapor transport. Journal of Crystal Growth 310 (2008) 2457–2463. [2] P. A. Tebbe, S.K. Loyalka, W. M. B. Duval. Finite element modeling of asymmetric and transient flowfields during physical vapor transport. Finite Elements in Analysis and Design 40 (2004) 1499-1519. [3] W. M. B. Duval, Convection in the physical vapor transport process-I: thermal, J. Chem. Vapor Deposition 2 (1994) 188-217. [4] W. M. B. Duval, Convection in the physical vapor transport process-II: thermosolutal, J. Chem. Vapor Deposition 2 (1994) 282-311. [5] D. W.Greenwell, B. L. Markham and F. Rosenberger. Numerical modeling of diffusive physical vapor transport in cylindrical ampoules, Journal of Crystal Growth, 51 (1981) 413-425. [6] R. B. Bird, W.E Stewart and E. M. Lightfoot. Transport Phenomena 2nd Ed., John Wiley & Sons Inc., (2002) 268, 353-356. [7] F.C. Moon. Chaotic and Fractal Dynamics. John Wiley & Sons Inc., (1992) 53-55.